Abstract:The evolution of microstructures for different hydrogen decrepitated routes was investigated in hydrogenation-disproportionation-desorption-recombination (HDDR) magnetic powders, with particular focus on the fracture of the SC heat-treated alloy during two-step hydrogen decrepitation (HD) and the influence of the first step temperature on magnetic properties. As the temperature increases, the properties of the magnetic powders increase and then decrease, the optimized performance of HDDR magnetic powders was obtained with B r =1.45 T, (BH) max =393 kJ·m −3 , DOA=0.79 when the first HD temperature is 65°C. The microscopic analysis shows that there are two problems in the one-step HD route: one is that the particle size is larger ∼150 μm and there are incomplete fractured cracks, the particle surface is more PrNd-rich phase, which leads to different reaction rates between the surface and center in HDDR particles, and the texture orientation of the fine grains at the edge of surface and crack is disordered. The second issue is that HD grains have significant angular difference with the c-axis orientation in incomplete fractured grain clusters, which is directly inherited by the HDDR magnetic powder, resulting in a misalignment texture. In comparison, the two-step HD process effectively addresses the issues derived from one-step HD process. Not only is the grain size of HDDR magnetic powders uniform and the width of the thin grain boundary phases (GBs) is less than the exchange coupling length, but also (Fe+Co) content exceeding 30 at% in GBs with weak magnetism. This is beneficial for enhancing exchange coupling effect between adjacent grains. Moreover, magnetic powder particle exhibits single-domain characteristics, which improves the grain texture orientation. This research provides a new insight for the development of high-orientation and high-performance HDDR magnetic powders.

Microstructure variation of Nd15Fe77B8 alloy in hydrogenation-disproportionation-desorption-recombination process

Microstructural Evolutions in Ndfe10.5mo1.5nx and Pr13fe80b7 Compounds During Hydrogenation-Disproportionation Desorption Recombination Process

In-Situ X-Ray Diffraction Study on Mlni(3.75)Co(0.75)Mn(0.3)Al(0.2) During Electrochemical Hydriding-Dehydriding Process

Microstructural Evolutions of Pr13fe80b7 Alloys During Solid Hddr Process

Preparation and microstructure features of nanocrystalline Nd12Fe82B6 alloy powder by a joint technique combining mechanical milling with HDDR

Microstructural changes during the disproportionation of Nd13Fe80B7 alloys

Preparation, Microstructure, and Magnetic Properties of A Nanocrystalline Nd12fe82b6 Alloy by Hddr Combined with Mechanical Milling

Characterization of the disproportionated NdFeCoZrB alloy by means of electron microscopy

Effects of the Disproportionation Stage of the HDDR Process on Magnetic Properties and Microstructure of Pr13Fe80B7 Alloys

Enhanced anisotropy of Pr-Nd-Fe-B HDDR magnetic powders by regulating the hydrogen decrepitated process

Self-Organized Nanorods in Disproportionated Sm2fe17 and Ndfe10.5mo1.5 Alloys

Anisotropic Characteristic in Hddr Nd13fe80b7

Rodlike Disproportionation Microstructure in the Pr13Fe80B7 Alloys Treated by Conventional HDDR Process

Nd2Fe14B/α-Fe Nanocomposites Prepared by Mechanically Activated Disproportionation and Subsequent Desorption-Recombination

The Effects of Hydrogen Disproportionation, Desorption, and Recombination on the Structure and Magnetic Properties of Sm2Fe17Nx and NdFe10Mo2Nx Compounds

Microstructure and magnetic properties of Nd2Fe 14B/α-Fe nanocomposite prepared by HDDR combined with mechanical milling

Anisotropy optimization of HDDR magnetic powders by precursor alloy annealing

Microstructure and Magnetic Properties of Nd2Fe14B/α-Fe Nanocomposite Prepared by HDDR Combined with Mechanical Milling

Effects of Additives on Hydrogen Absorption and Desorption Characteristics of Nd(Fe, Mo)(12) Alloys

Effects of Misalignment of c-axis on the Properties of Hydrogenation–Disproportionation–Desorption–Recombination Particles

Microstructures And Hydrogen Desorption Properties Of The Mgh2-Alh3 Composite With Nbf5 Addition