Abstract:The present study investigates the formation mechanism of black spot defects on the surface of industrial continuously hot-dip galvanized Zn-2Al-1.5Mg coatings. Electrochemical experiments and neutral salt spray tests are conducted to study the corrosion resistance of the black spot defects and their influence on the corrosion mechanism of the coatings. The results show that the enrichment of Mg elements within the coating is the fundamental cause of the formation of this defect. The enrichment of Mg elements leads to a reduction in the size of primary Zn, an increase in the proportion of eutectic structures and the MgZn 2 within the defective coatings. Consequently, the defective coatings exhibit the higher surface hardness and, after skin pass rolling, display the different reflective properties compared to surrounding coatings. The black spots feature is attributed to the formation of oxide film containing MgO. The electrochemical test results indicate that black spot defect exhibits enhanced corrosion resistance due to the lower Volta potential difference (VPD) between each phase on its surface. Moreover, the fine and dispersed cathodes not only avoid the occurrence of extremely pH sites, but also facilitate the formation of uniform distributed corrosion products with high protective ability. In the 600-h neutral salt spray experiments, Zn-2Al-1.5Mg coatings with black spot defects exhibit enhanced corrosion resistance, which is attributed to the Mg enrichment delaying the decomposition of highly protective corrosion products.

Study on Passivation Coating Corrosion Resistance of Continuous Hot Dip Galvanizing Strip

Study on environment-friendly passivation for hot-dip galvanized steel with high corrosion resistance

Passivation of hot-dip galvanized zinc-5％ aluminum alloy coating in a silicate solution

A Research on the Corrosion Resistance of Phytic Acid Passivating Coatings for Galvanized Parts

Anti-corrosion Performance of Molybdate Composite Passivation Film on Hot-Dip Galvanized Steel

Corrosion Behavior of Hot-dip Galvanized Steel in Simulated Acid Rain Environment

Production Technology of Hot Dip Zincing and Research Status for Passivation Thereof

Study on the formation and corrosion mechanism of black spot defects on the surface of industrial continuously hot-dip galvanized Zn-2Al-1.5Mg coating

Corrosion Properties of Steel Sheet with Zinc-base Alloyed Coatings

A Review of Recent Developments in Coating Systems for Hot-Dip Galvanized Steel

Electron Microscopic Characterization of Corrosion Products on Surface of Galvanized Steel Sheet

Growth and Corrosion Behavior of Molybdate Passivation Film on Hot Dip Galvanized Steel

Preparation and Characterization of Cr-free passivation films on zinc coating using Response Surface Methodology and Electrochemical Methods

The Study Development of Corrosion in Molten Zinc Bath

Microstructure and Corrosion Resistance of Hot-Dipped Zn-Ti Coating

Preparation of Phytic Acid/Silane Composite Passivation Coating on Hot-Dip Zinc Sheet and Its Corrosion Resistance

Research progress of silicate and silane passivation mechanisms for galvanized steel

A review of physical properties of hot-dip galvanized coating layer by layer and their respective electrochemical corrosion behavior

ANALYSES OF FORMATION OF WHITE RUST ON HOT DIP GALVANIZED STEEL AND RELEVANT COUNTERMEASURES

Trivalent Chromium Passivation Process for Zinc Coating

Study on the Preparation and Corrosion Resistance Properties of Superhydrophobic Coatings on Galvanized Steel