Fabrication and characterization of particle-stacking microporous nickel using laser powder bed fusion
Jinyong Qiu,Xiaoqiang Xu,Xu Chen,Yaxiong Liu,Yanlong Wu
DOI: https://doi.org/10.1016/j.mtcomm.2024.108763
IF: 3.8
2024-06-01
Materials Today Communications
Abstract:Nickel (Ni) and nickel-based materials with specific pore configurations, particularly interconnected micropores as channels, have significant potential in new energy technologies. Laser 3D printing is a simple, rapid, and effective method for one-step formation; however, challenges remain in the fabrication of micropores (< 50 μm). This study successfully designed a particle-to-particle stacking microporous nickel structure using laser energy to regulate the melting and fusion behaviors of nickel particles. While laser power had a minimal effect on the pore size, it significantly impacted the porosity. The formation of interconnected pores depended on a large hatch distance and high laser scanning speed, while the latter also contributed to the creation of uniform micropores characterized by narrow sintered bands. The particle-stacking microporous nickel exhibited a homogeneous pore distribution, with pore sizes ranging from approximately 10 to 50 μm in both mean pore size and median pore size (D50), along with a high percentage size distribution in 1 – 10 μm. Furthermore, it displayed controllable porosities between 18.44% and 52.94%, along with remarkable resistance to deformation and superior compressive performance, featuring a high yield strength exceeding 50 MPa compared to the conventionally-processed porous nickels.
materials science, multidisciplinary