Abstract:To improve the comprehensive performance of aluminum alloy and expand its application range, a laser cladding technology was used to a prepare Ni-Cr-B-Si alloy cladding layer, adding 4% CeO2, 5% Y2O3, and 5% La2O3 on the surface of 6063Al. The distribution of elements, the nucleation and growth mechanism of the interface transition and upper cladding layers, and the action mechanism of rare earths were analyzed from the thermodynamics, kinetics, and solidification perspectives. Results show that the cladding layer is mainly composed of a thin interface transition layer at the bottom and a thick cladding layer at the top. There are numerous pores and cracks in the interface transition layer of the Ni-Cr-B-Si cladding layer, part of the cladding layer is peeled off, and the structure is obviously segregated. However, the cladding layer adding with 4% CeO2, 5% Y2O3 and 5% La2O3 has no obvious pores, cracks and shedding, its grain distribution is more dispersed, and the structure is refined. The organization state from good to poor follows the order Ni60 + 4%CeO2 cladding layer, Ni60 + 5%Y2O3 cladding layer, and Ni60 + 5%La2O3 cladding layer. It was found through research that the addition of rare earth can improve the fluidity of the molten pool during the solidification of the cladding layer and purify the molten pool, and most of the rare earths are segregated at the grain boundary and phase boundary, which strengthens the grain boundary and phase boundary. The strengthening mechanism of the cladding layer is solid solution strengthening and fine grain strengthening, and the Ni60 + 4% CeO2 cladding layer also has a strengthening mechanism of dispersion strengthening.

Comparison of laser-clad and furnace-melted Ni-based alloy microstructures

Investigation on the Microstructure and Mechanical Behaviors of a Laser Formed Nb-Ti-Al Alloy

Microstructures of laser-clad nickel-based hardfacing alloys

Microstructure of Laser Clad Ni-based Alloy and Ni+Cr3 C2 Composite Coatings

Effect of Ni Content on the Structure and Properties of Laser Surface Clad Ni-Fe Based Alloys

Amorphous Structure in Laser Clad Ni-Cr-Al Coating on Al-Si Alloy

Nucleation and strengthening mechanism of laser cladding aluminum alloy by Ni-Cr-B-Si alloy powder based on rare earth control

Microstructure of Bonding Zones in Laser-Clad Ni-Alloy-Based Composite Coatings Reinforced with Various Ceramic Powders

The microstructure and tribological characteristics of laser-clad Ni–Cr–Al coatings on aluminium alloy

Microstructure and performance optimization of laser cladding nano-TiC modified nickel-based alloy coatings

Microstructures and properties of nano-modified multimodal Cr3C2-NiCr coatings made through laser cladding

Amorphization of Fe-Ni Based Alloys by Laser Cladding and Remelting

Evolution of microstructure of Al particle-reinforced NiCoCrAlY coatings fabricated on 304 stainless steel using laser cladding

Microstructural Characterisation of Laser Clad Coating of Nickel Based Alloy with Dissolved Sicp

Effect of process parameters and niobium carbide addition on microstructure and wear resistance of laser cladding nickel‐based alloy coatings

Influence of the Materials on the Solidification Microstructure of Laser Multi-Layer Cladding

Microstructure and Wear Properties of Laser Processed Ni Based Amorphous Matrix Coatings

Cracking Behavior of Laser Cladding Forming Nickel Based Alloys

Layered Microstructure Distribution and Forming Mechanism of Laser-Processed Ni-Fe-B-Si-Nb-C Amorphous Composite Coatings

Experimental Study of the Microstructure and Micromechanical Properties of Laser Cladded Ni-based Amorphous Composite Coatings

Microscopic Morphology and Microstructure of Ti-N and Ti-Ni Phase Between the Dilution Zone and the Clad Zone in Laser Remelting Nicrbsi/Tin Layer on Ti-6al-4v Alloy Surface