Abstract:We report herein a typical piezoelectric polymer, poly(vinylidene fluoride) (PVDF) to be successfully wrapped on single-walled carbon nanotubes (SWCNTs) using a simple supercritical carbon dioxide (SC CO(2)) antisolvent-induced polymer epitaxy method. Our study focused on the effect of different solvents on the morphology of PVDF wrapping on SWCNTs. Three organic solvents, dimethyl sulfoxide (DMSO), N,N-dimethylformamide (DMF), and N,N-dimethylacetamide (DMAc) were chosen for PVDF. When DMSO was used as solvent, the decorating degree of PVDF on the surface of SWCNTs increases significantly with the increase of SC CO(2) pressure, and nanocrystals wrapping on SWCNTs can be observed at high pressure. FTIR and Raman spectra indicated that there exist interactions between SWCNTs and PVDF chains. What's more, FTIR results also show that there exists a transformation from the beta-phase to the alpha-phase of PVDF in DMSO with the assistance of SC CO(2), which is similar to the action of elongation/shear flow field. It indicated that the alpha-phase is the predominant form occurring on the surface of SWCNTs after treatment with SC CO(2). And the helical structure on SWCNTs observed from the TEM image reflected the alternate trans- and gauche-bond conformation of the alpha-form. When DMF or DMAc was used as the solvent, although nanocrystal wrapping and helical structure was not visible, the samples had more excellent dispersion than that in DMSO. Particularly, for DMF, a typical network structure was observed, which is similar to a spider web. Therefore, this work supplies a clue that the various morphologies of nanohybrid structure can be obtained just by changing the solvent during the treatment process of SC CO(2), and accordingly, the tailored nanohybrid structure are promising and important for functional design as a basic component in microfabrication and other fields.

Effective Polymerization of C-60 in Swnts under High Pressure and Simultaneous Uv Light Irradiation

High-pressure induced polymerization of C60 nanorods

High Pressure and High Temperature Induced Polymerization of C60 Nanotubes

Raman Spectroscopy Study of Carbon Nanotube Peapods Excited by Near-Ir Laser under High Pressure

Rotational Dynamics of Confined C 60 from Near-Infrared Raman Studies under High Pressure

Comparative Study of Pressure-Induced Polymerization in C-60 Nanorods and Single Crystals

High pressure and high temperature induced polymeric C60 nanocrystal

High Pressure Raman Study of Single-Wall Carbon Nanotubes

Pressure-induced polymerization of nano- and submicrometer C60 rods into a rhombohedral phase

High Pressure and High Temperature Induced Polymeric C60 Nanorods and Their Photoluminescence Properties

In situ Raman and photoluminescence study on pressure-induced phase transition in C 60 nanotubes

Photoluminescence Properties Of High-Pressure-Polymerized C-60 Nanorods In The Orthorhombic And Tetragonal Phases

Modification of carbon nanotubes using poly(vinylidene fluoride) with assistance of supercritical carbon dioxide: the impact of solvent

Synthesis and Raman scattering study of double-walled carbon nanotube peapods

High Pressure and High Temperature Induced Polymerization of C60 Quantum Dots

High Pressure and High Temperature Induced Polymerization of Doped C60 Materials

Pressure Induced Metastable Polymerization in Doped C60 Materials

Amorphization of C-60 Nanotubes under Pressure

Exploring the Possible Interlinked Structures in Single‐wall Carbon Nanotubes under Pressure by Raman Spectroscopy

Synthesis And High Pressure Induced Amorphization Of C-60 Nanosheets

Low temperature fullerene encapsulation in single wall carbon nanotubes: synthesis of N@C$_{60}$@SWCNT