Abstract:Ordered amorphous carbon clusters (OACC) transformed from m-xylene solvated C60 (C60·m-xylene) are known as the first crystalline material constructed from amorphous building blocks and have attracted a lot of attention. The formation mechanism and physical properties of this material are of great importance for the design of more materials with such structural characteristics. In this article, the transport and structural properties of C60·m-xylene are systematically investigated under pressure using impedance spectroscopy, four-probe resistance measurements, and Raman spectroscopy. It is found that C60·m-xylene is an insulator at ambient pressure. The resistance decreases sharply starting at the pressure around 8 GPa due to the pressure-induced dimerization of C60 verified by the Raman study. The presence of solvent hinders further polymerization of C60 under higher pressures. The temperature-dependence of resistance exhibits a semiconducting characteristic at > 8–26.9 GPa, and is well described by Mott’s three-dimensional variable-range hopping model (3D-VRH), indicating an insulating-to-semiconducting transition accompanied with pressure-induced dimerization. The resistance and hopping energy are both found to decrease monotonically with pressure and reach the minimum near 24 GPa. Above the pressure, resistance and hopping energy values start to rise, suggesting a transition to another semiconducting state, which is attributed to the pressure-induced formation of OACC. The conductivity shows a large hysteresis during decompression from higher than 24 GPa, confirming a different transport behavior of the sample with retained fullerenes versus OACC. The findings of our study suggest that the transport property of fullerene is tunable by introducing solvates and further enhance our understanding of the OACC.

Pressure Induced Metastable Polymerization in Doped C60 Materials

High Pressure and High Temperature Induced Polymerization of Doped C60 Materials

Reversible Polymerization in Doped Fullerides under Pressure: the Case of C-60(Fe(C5h5)(2))(2)

High Pressure and High Temperature Induced Polymerization of C60 Nanotubes

Investigation of the Polymerization Mechanism of Ferrocene Doped C60 under High Pressure and High Temperature

Pressure-induced polymerization of nano- and submicrometer C60 rods into a rhombohedral phase

High Pressure and High Temperature Induced Polymerization of C60 Quantum Dots

Comparative Study of Pressure-Induced Polymerization in C-60 Nanorods and Single Crystals

In situ Raman and photoluminescence study on pressure-induced phase transition in C 60 nanotubes

High pressure and high temperature induced polymeric C60 nanocrystal

Pressure-Induced Diversity of Π-Stacking Motifs and Amorphous Polymerization in Pyrrole

High Pressure and High Temperature Induced Polymerization of C60 Solvates: the Effect of Intercalated Aromatic Solvents

High Pressure and High Temperature Induced Polymeric C60 Nanorods and Their Photoluminescence Properties

Reversible Pressure-Induced Polymerization of Fe(C5H5)2 Doped C70

Quasi 3D Polymerization in C60 Bilayers in a Fullerene Solvate

Amorphization of C-60 Nanotubes under Pressure

Effective Polymerization of C-60 in Swnts under High Pressure and Simultaneous Uv Light Irradiation

Electronic Structures in C60-Polymers (review)

Doping Effects and Electronic States in C60-Polymers

Photoluminescence Properties Of High-Pressure-Polymerized C-60 Nanorods In The Orthorhombic And Tetragonal Phases

Tunable electrical properties of C60·m-xylene and the formation of semiconducting ordered amorphous carbon clusters under pressure