Abstract:Cerium dioxide (CeO2) nanoparticles were synthesized by sol–gel-based hydrothermal method. During synthesis, cerium(III) chloride heptahydrate (CeCl3⋅7H2O) was used as cerium source; ammonia (NH3), tetraethylammonium hydroxide (C8H21NO), tetra-n-butyl ammonium hydroxide (C16H37NO), benzyl trimethyl ammonium hydroxide (C10H17NO) and benzyl triethyl ammonium hydroxide (C13H23NO) ionic liquids were used as catalyst, deionized water (H2O) was used as hydrolysis agent and solvent, and 2-aminopropanoic acid (C3H6NO2) was used as stabilizing agent. The nano-CeO2 particles were characterized by several techniques X-ray diffractometer (XRD), particle size analyzer, Branauer–Emmett–Teller analyzer (BET), ultraviolet–visible spectrophotometer (UV–Vis), transmission electron microscope (TEM). XRD characterization confirms that CeO2 crystals were analyzed as cubic fluorite structure. The full width at half maximum (FWHM) values referring to [111] lattice planes of CeO2 indicate a decrease in crystallinity associated with different bases used during synthesis of particles. Small sized crystals were formed in weak ionization degree and branched structures. As the crystallite size decreases, both agglomeration and the hydrodynamic diameter increases as expected. The size distribution of nano-CeO2 particles obtained by precipitation using different bases with a pH of 10 decreases from 25.92 to 20.57 nm. The size of nanoparticles prepared using ammonia at pH 9 and 8 are 15.60 and 9.50 nm, respectively. The most significant surface area change occurred in particles obtained using benzyl trimethyl ammonium hydroxide (BTMAH) and benzyl triethyl ammonium hydroxide (BTEAH). Such a significant reduction in surface area is believed to be due to the agglomeration or aggregation of particles with small crystallite size, resulting in smaller sized crystals as the alkyl group chain length and branching increase. These irregularities may result from the agglomeration and formation of large clusters observed by the TEM. The obtained CeO2 nanoparticles are crystalline and can readily be dispersed in water without any additional processing or surfactant agent. Well-defined strong absorbance peak located at 200–800 nm was observed for all samples. The bandgap increases with the decrease in particle size, meaning that smaller particles exhibit better UV absorption. The fact that the particles obtained in the presence of BTMAH and BTEAH cut off longer wavelength proved that it is due to lower bandgap energies.Graphical abstract

Synthesis and Photochemical Properties of White Calcia-Doped Ceria Nanoparticles Via Soft Solution Processes

Synthesis and characterization of ceria nanoparticles by complex-precipitation route

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Preparation, Phase Transformation and Photocatalytic Activities of Cerium-Doped Mesoporous Titania Nanoparticles

Facile Alcohothermal Synthesis, Size-Dependent Ultraviolet Absorption, and Enhanced CO Conversion Activity of Ceria Nanocrystals

Preparation of Nanocrystalline Ceria Particles by Sonochemical and Microwave Assisted Heating Methods

Synthesis of porous silica gel and study on the adsorption of cerium

Preparation of ceria by combined sol–gel and hydrothermal method: insights from the effects of different bases on the particle size distribution

General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties

Enhanced Artificial Enzyme Activities on the Reconstructed Sawtoothlike Nanofacets of Pure and Pr-Doped Ceria Nanocubes

Synthesis of Fibrous Micro-nano Hierarchical Porous Cerium Dioxide Materials by the Impregnation and Thermal Decomposition Method and Its Enhanced Photocatalytic Activity

Synthesis and Characterization of Nanoscaled Cerium (IV) Oxide Via a Solid‐State Mechanochemical Method

Improving the Photocatalytic Performance of Porous Ceria under Visible Light Illumination via Mn Incorporation

Dimension-Manipulated Ceria Nanostructures (0d Uniform Nanocrystals, 2d Polycrystalline Assembly, and 3d Mesoporous Framework) from Cerium Octylate Precursor in Solution Phases and Their Co Oxidation Activities

Preparation of Discrete Nanosize Ceria Powder

Preparation of Ceria with Large Particle Size and High Appearance Density

Nanoceria synthesis in molten KOH-NaOH mixture: Characterization and oxygen vacancy formation

Novel synthesis of cerium oxide nano photocatalyst by a hydrothermal method

Solventless synthesis of cerium oxide nanoparticles and their application in UV protective clear coatings

Control Of Chemical State Of Cerium In Doped Anatase Tio2 By Solvothermal Synthesis And Its Application In Photocatalytic Water Reduction