Influence of Si Contents on Microstructures and Mechanical Properties of High Strength and Toughness 7050 Aluminum Alloys

ZHANG Ke-wei,SHE Huan,LIU Hong-liang,SHU Da,WANG Jun

2013-01-01

Abstract:Eight kinds of 7050aluminum alloys with different Si contents have been prepared by cast.The influence of Si contents from 0.033%to 0.491%on microstructures and mechanical properties has been investigated.The results show that significant coarse Si-rich impurity phase has been found in as-cast microstructures when Si content is increased to 0.134%,and the content of this phase is increased with Si content increasing.The coarse Si-rich impurity phases are insoluble during homogenizing annealing,hot extrusion and solution treatment,and remain in aged microstructures of alloys.The aged alloy with 0.134% Si has the highest tensile strength and plasticity at room temperature.The strength,plasticity and fracture toughness reduce significantly when Si content is higher than 0.344%.Si content should be controlled in the range of 0.121%to 0.134%to get the best strength and plasticity.To obtain a better fracture toughness,the Si content in the alloy should be further reduced.