Abstract:The material accumulation during roasting in the practical production causes the hypoxia of the internal materials, leading to the relatively lower vanadium recovery than that in theoretical studies. This work aims to solve the problem of material hypoxia through the Na2O2-briquetting roasting route. The vanadium slag and Na2O2 powders were mixed, briquetted, and roasted at various parameters. The generated phases and their distributions were analyzed using X-ray diffraction, Fourier transform infrared spectroscopy, and electron probe microanalysis. The analyzing results showed that Fe2O3, Fe3O4, Mg0.165Mn0.835O, CaTiO3, and Na3VO4 were generated during roasting. The solid–solid reaction between V2O5 and Na2O was described using the vacancy-mediated diffusion mechanism. Na+ (or V5+), in the Na2O (or V2O5) layer, jumped and diffused through the Na+ (or V5+) vacancies (in the Na3VO4 layer) to the Na3VO4/V2O5 (or Na3VO4/Na2O) interface. Na+ (or V5+) reacted with V2O5 (or Na2O) and O2 decomposed from Na2O2 or transported from the air to generate Na3VO4. The roasted mixture was leached in an aqueous solution to study the effects of the roasting variables on the vanadium leaching recovery. The vanadium leaching recovery was very sensitive to the roasting variables, it showed very complicated relationships with the Na/V molar ratio, temperature, time, and briquetting pressure. The maximum vanadium leaching recovery of 95.57 pct was achieved when the Na/V molar ratio, temperature, time, and pressure were optimized as 3/1, 850 °C, 2.5 hours, and 5 MPa, respectively. The leaching solution containing vanadium was processed via precipitation and calcination to gather vanadium. The obtained compound was identified as V2O5 with a purity of 96.84 pct, based on the high consistency of diffraction peaks between the present work and that of the joint committee on powder diffraction standards.

The Research on New-Style Composite Additives Reburning for Extractingvanadium from Ash of Stone Coal

Influential Factors of Vanadium Extraction by Reburning and Dilute Sulfuric Acid Leaching of Ash of Stone Coal

Calcination Characteristics of Vanadium-containing Stone Coal Ball in Circulating Fluidized Bed

Recovery of vanadium from vanadium slag by composite additive roasting–acid leaching process

The Investigate of Vanadium-Containing Slurry Oxidation Roasting Process for Vanadium Extraction

Vanadium Extraction from Stone Coal Using a Novel Two-Stage Roasting Technology

Investigation of Vanadium-Containing Sludge Oxidation Roasting Process for Vanadium Extraction

Clean and efficient extraction of vanadium from vanadium slag: Effect of manganese on the phase composition and vanadium extraction process

Selective recovery of vanadium from high-chromium vanadium slag by a mechanically activated low-sodium salt roasting-water leaching process

Extraction of Vanadium Pentoxide from Stone Coal Pellets by Roasting in a Fluidized Bed Combustor

Effect of chromium content on the phase composition, crystallization and components extraction of vanadium slag

Phase Transition and Vanadium Leaching Mechanism during Roasting of Vanadium‐Bearing Rock Coals

Review of Vanadium Extraction from Stone Coal by Roasting Technique with Sodium Chloride and Calcium Oxide

Extraction of Vanadium From Vanadium Slag Through a New Technique Route Including Na2O2-Briquetting Roasting Process

Recovery of vanadium from vanadium slag by composite roasting with CaO/MgO and leaching

Elemental Distribution Modification Toward Target Calcium Roasting of Vanadium-Bearing Slags

Acid Leaching for Extracting Vanadium from Residue of High-Carbon Stone Coal after CFB Combustion

Cleaner extraction of vanadium from vanadium-chromium slag based on MnO2 roasting and manganese recycle

Non-salt roasting mechanism of V–Cr slag toward efficient selective extraction of vanadium

Extraction of vanadium from black shale by novel two-step fluidized roasting process

Investigations on the microwave absorption properties and thermal behavior of vanadium slag: Improvement in microwave oxidation roasting for recycling vanadium and chromium