Elemental Distribution Modification Toward Target Calcium Roasting of Vanadium-Bearing Slags

Yongqi Sun,Xingyue Ma,Mao Chen,Xiaodong Ma

DOI: https://doi.org/10.1007/s11837-024-06603-5

2024-05-18

JOM

Abstract:The elemental distributions among various phases in vanadium-bearing slags have been quantified toward high-efficiency separation and extraction by calcium roasting using electron probe X-ray microanalysis. The roles of the roasting conditions were clarified, including roasting temperature, roasting time, and calcium amount. It was found that, with increasing roasting temperature, the V 2 O 5 concentration in the target vanadium-enriched phase, predominantly in a form of 2(Ca,Mn)O·V 2 O 5 , decreased along with more SiO 2 and Fe 2 O 3 in this phase; while, with increasing roasting time, the V 2 O 5 concentration in the vanadium-enriched phase increased due to a more complete reaction. However, a higher calcium addition induced a lower V 2 O 5 concentration in the vanadium-enriched phase and, therefore, a CaO/V 2 O 5 weight ratio of 0.6 was employed. In addition to the vanadium-enriched phase, the solubilities, especially V 2 O 5 in the SiO 2 and Fe 2 O 3 solid solutions under varying roasting conditions, were also identified for a reduction of vanadium loss. Based on those quantitative results, the main principles to target to adjust the elemental distributions among various phases during the calcium roasting of vanadium-bearing slags are discussed toward a low-cost and high-efficiency vanadium extraction.

materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy