Abstract:The material accumulation during roasting in the practical production causes the hypoxia of the internal materials, leading to the relatively lower vanadium recovery than that in theoretical studies. This work aims to solve the problem of material hypoxia through the Na2O2-briquetting roasting route. The vanadium slag and Na2O2 powders were mixed, briquetted, and roasted at various parameters. The generated phases and their distributions were analyzed using X-ray diffraction, Fourier transform infrared spectroscopy, and electron probe microanalysis. The analyzing results showed that Fe2O3, Fe3O4, Mg0.165Mn0.835O, CaTiO3, and Na3VO4 were generated during roasting. The solid–solid reaction between V2O5 and Na2O was described using the vacancy-mediated diffusion mechanism. Na+ (or V5+), in the Na2O (or V2O5) layer, jumped and diffused through the Na+ (or V5+) vacancies (in the Na3VO4 layer) to the Na3VO4/V2O5 (or Na3VO4/Na2O) interface. Na+ (or V5+) reacted with V2O5 (or Na2O) and O2 decomposed from Na2O2 or transported from the air to generate Na3VO4. The roasted mixture was leached in an aqueous solution to study the effects of the roasting variables on the vanadium leaching recovery. The vanadium leaching recovery was very sensitive to the roasting variables, it showed very complicated relationships with the Na/V molar ratio, temperature, time, and briquetting pressure. The maximum vanadium leaching recovery of 95.57 pct was achieved when the Na/V molar ratio, temperature, time, and pressure were optimized as 3/1, 850 °C, 2.5 hours, and 5 MPa, respectively. The leaching solution containing vanadium was processed via precipitation and calcination to gather vanadium. The obtained compound was identified as V2O5 with a purity of 96.84 pct, based on the high consistency of diffraction peaks between the present work and that of the joint committee on powder diffraction standards.

Recovery of vanadium from vanadium slag by composite roasting with CaO/MgO and leaching

Recovery of vanadium from vanadium slag by composite additive roasting–acid leaching process

Efficient Recovery of Vanadium from High-Chromium Vanadium Slag with Calcium-Roasting Acidic Leaching

Direct recovery of low valence vanadium from vanadium slag —— Effect of roasting on vanadium leaching

Efficient Vanadium Extraction from Vanadium Slag by Roasting-Free Assisted Acid Leaching: Pure Oxygen Oxidation of Molten Vanadium Slag

Selective recovery of vanadium from high-chromium vanadium slag by a mechanically activated low-sodium salt roasting-water leaching process

Clean and efficient extraction of vanadium from vanadium slag: Effect of manganese on the phase composition and vanadium extraction process

Cleaner extraction of vanadium from vanadium-chromium slag based on MnO2 roasting and manganese recycle

Process and Kinetic Assessment of Vanadium Extraction from Vanadium Slag Using Calcification Roasting and Sodium Carbonate Leaching

Novel Understanding of Simultaneous Extraction of Vanadium and Manganese from Vanadium Slag and Low-Grade Pyrolusite Based on Selective Oxidation–Reduction Roasting

Vanadium extraction from water-cooled vanadium converter slag via salt-free roasting and acid leaching

Extraction of Vanadium From Vanadium Slag Through a New Technique Route Including Na2O2-Briquetting Roasting Process

Magnesiation roasting-acid leaching: A zero-discharge method for vanadium extraction from vanadium slag

Clean process for vanadium extraction from vanadium-bearing converter slag

Non-salt roasting mechanism of V–Cr slag toward efficient selective extraction of vanadium

A new process for extracting vanadium by direct calcification using the heat of molten vanadium slag

Review of leaching, separation and recovery of vanadium from roasted products of vanadium slag

Recovery of Valuable Elements from Molten Vanadium Slag Through High-Temperature Reduction

A review on the roasting-assisted leaching and recovery of V from vanadium slag

Extraction of vanadium from vanadium slag by sodium roasting-ammonium sulfate leaching and removal of impurities from weakly alkaline leach solution

An efficient utilization of high chromium vanadium slag: Extraction of vanadium based on manganese carbonate roasting and detoxification processing of chromium-containing tailings