Direct Dehydrogenation of Methanol to Formaldehyde over Novel Ag-Containing Ceramics

Y Dong,WL Dai,JL Li,JF Deng

DOI: https://doi.org/10.1246/cl.2001.534

2001-01-01

Chemistry Letters

Abstract:A novel silver-ceramics supported catalyst showing excellent activity and selectivity in the direct dehydrogenation of methanol to formaldehyde was prepared. The selectivity was as high as 100% and the yield of formaldehyde reached 70%.

What problem does this paper attempt to address?

A new silver-containing ceramics for catalytic oxidation of methanol to formaldehyde

Jia-Liang Li,Wei-Lin Dai,Yi Dong,Jing-Fa Deng

DOI: https://doi.org/10.1016/S0167-577X(00)00034-3

IF: 3

2000-01-01

Materials Letters

Abstract:A new silver-containing (20 wt.%) ceramics has been prepared by impregnating natural kaolin with silver nitrate following high-temperature annealing. The catalyst exhibits excellent activity and selectivity during the methanol oxidation to formaldehyde with the yield of up to 89.3%. Before reaction, the silver in the catalyst is present in an extremely thermally stable ionic state incorporated within the framework of the ceramics. Upon catalytic reaction, well-dispersed metallic silver (particle size ~800 nm) are obtained on the surface of the ceramic support owing to the chemical reduction. The high formaldehyde yield of the catalyst is due to the positive charge on silver.
Direct Dehydrogenation of Methanol to Formaldehyde over Pre-Treated Polycrystalline Silver Catalyst

Li-Ping Ren,Wei-Lin Dai,Xin-Li Yang,Jian-Hua Xu,Yong Cao,Hexing Li,Kangnian Fan

DOI: https://doi.org/10.1007/s10562-004-0780-6

IF: 2.936

2005-01-01

Catalysis Letters

Abstract:The polycrystalline silver after pre-treated with oxygen at high temperature was found to show excellent activity and selectivity in the process of direct dehydrogenation of methanol to anhydrous formaldehyde and the active oxygen species for this reaction was observed and proposed as the active centeres with in situ Raman scattering.
First Observation of Highly Efficient Dehydrogenation of Methanol to Anhydrous Formaldehyde over Novel Ag–SiO2–MgO–Al2O3catalyst

Li-Ping Ren,Wei-Lin Dai,Yong Cao,Hexing Li,Kangnian Fan

DOI: https://doi.org/10.1039/b310316a

2003-01-01

Abstract:Novel Ag-SiO2-MgO-Al2O3 catalyst prepared by sol-gel method showed extremely high activity and selectivity (both equal to 100%) in the direct dehydrogenation of methanol to anhydrous formaldehyde.
Novel Highly Active Ag–SiO 2 –MgO Catalysts Used for Direct Dehydrogenation of Methanol to Anhydrous Formaldehyde

Li-Ping Ren,Wei-Lin Dai,Yong Cao,Kang-Nian Fan

DOI: https://doi.org/10.1023/A:1022172808752

IF: 2.936

2003-01-01

Catalysis Letters

Abstract:Direct dehydrogenation of methanol to anhydrous formaldehyde was carried out over a novel Ag-SiO 2 -MgO catalyst prepared by the sol-gel method. The catalytic activity was measured over the temperature interval 350-700 °C and the space velocity of 1 × 10 4 h -1 , while the optimum conditions were found to be 20 wt% loading of silver and 650 °C reaction temperature. The catalyst exhibits excellent activity (96% conversion) and selectivity (78%) during the process of dehydrogenation with the yield of formaldehyde up to 75%. X-ray diffraction patterns for the novel Ag(20 wt%)-SiO 2 -MgO catalyst correspond to α-crystobalite(100) and Ag(111), (200), (220), (311) and (222). Scanning electron microscopy was used to determine the morphology and particle size. Isolated silver particles with a mean size of about 5 μm were observed on the surface of the catalyst.
Highly active Ag-SiO2-Al2O3 catalyst used for the dehydrogenation of methanol to anhydrous formaldehyde

LiPing Ren,Weilin Dai,Yong Cao,Hexing Li,Wenhua Zhang,Kangnian Fan

DOI: https://doi.org/10.3321/j.issn:0567-7351.2003.06.023

2003-01-01

Acta Chimica Sinica

Abstract:The sol-gel method was applied to prepare a novel Ag-SiO 2-Al2O3 catalyst which showed high activity in the reaction of direct dehydrogenation of methanol to formaldehyde. The influence of silver loading, calcination temperature and reaction temperature on the catalytic activity was investigated, respectively. XRD patterns show that there are no sharp diffraction peaks before reaction, but after reaction, a set of sharp peaks corresponding to Ag(111), Ag(200), Ag(220), Ag(311) and Ag(222) are observed. SEM results accord well with those from XRD. The special structure of the novel Ag-SiO2-Al2O3 catalyst may lead to its excellent catalytic performance (95.0% of conversion of methanol and 81.2% of HCHO yield), which is the best of all the previous results.
First observation of highly efficient dehydrogenation of methanol to anhydrous formaldehyde over novel Ag-SiO2-MgO-Al2O 3 catalyst

LiPing Ren,Weilin Dai,Yong Cao,Hexing Li,Kangnian Fan

DOI: https://doi.org/10.1039/b310316a

IF: 4.9

2003-01-01

Chemical Communications

Abstract:Novel Ag-SiO2-MgO-Al2O3 catalyst prepared by sol-gel method showed extremely high activity and selectivity (both equal to 100%) in the direct dehydrogenation of methanol to anhydrous formaldehyde.
Novel Sol–gel‐derived Ag/SiO2–Al2O3 Catalysts for Highly Selective Oxidation of Methanol to Formaldehyde

Wei‐Lin Dai,Jia‐Liang Li,Yong Cao,Qin Liu,Jing‐Fa Deng

DOI: https://doi.org/10.1023/a:1019066415748

IF: 2.936

2000-01-01

Catalysis Letters

Abstract:Novel Ag/SiO2–Al2O3 catalysts with low silver content prepared by the sol–gel method exhibit excellent catalytic properties in the catalytic oxidation of methanol to formaldehyde. The silver content was as low as 2% and the yield of formaldehyde was achieved as 90.3%, which is 16% higher than that of pumice‐supported silver and even 5–6% higher than that of a commercial electrolytic silver catalyst. XRD, XPS and SEM results reveal that all silver was present as Ag+ before catalytic reaction and was partially reduced to the metallic state after the reaction. It was also found that silver was aggregated on the surface after its reduction.
Novel sol–gel‐derived Ag/SiO 2 –Al 2 O 3 catalysts for highly selective oxidation of methanol to formaldehyde

Wei‐Lin Dai,Jia‐Liang Li,Yong Cao,Qin Liu,Jing‐Fa Deng

DOI: https://doi.org/10.1023/A:1019066415748

IF: 2.936

2000-01-01

Catalysis Letters

Abstract:Novel Ag/SiO 2 –Al 2 O 3 catalysts with low silver content prepared by the sol–gel method exhibit excellent catalytic properties in the catalytic oxidation of methanol to formaldehyde. The silver content was as low as 2% and the yield of formaldehyde was achieved as 90.3%, which is 16% higher than that of pumice‐supported silver and even 5–6% higher than that of a commercial electrolytic silver catalyst. XRD, XPS and SEM results reveal that all silver was present as Ag + before catalytic reaction and was partially reduced to the metallic state after the reaction. It was also found that silver was aggregated on the surface after its reduction.
A Novel Silver-Silica Catalyst Used for the Manufacture of Formaldehyde

WL Dai,Y Cao,HX Li,JF Deng

DOI: https://doi.org/10.1246/cl.1997.197

1997-01-01

Chemistry Letters

Abstract:Several novel silver-silica catalysts were prepared by means of sol-gel method, which exhibited high activity and selectivity in the catalytic oxidation of methanol to formaldehyde. The optimum content of silver was determined as 20%(w/w.), which showed 97% conversion and 85.5% yield of formaldehyde. Some other superiority of the as-prepared silver catalysts was observed by comparing with the commercial silver catalysts, including pumice-supported silver and electrolytic silver. XRD patterns reveal that silver is present as a crystalline state in the Ag-SiO2 catalysts.
First observation of highly efficient dehydrogenation of methanol to anhydrous formaldehyde over novel Ag?SiO2?MgO?Al2O3 catalystElectronic supplementary information (ESI) available: XRD and SEM. See http://www.rsc.org/suppdata/cc/b3/b310316a/

Li-Ping Ren,Wei-Lin Dai,Yong Cao,Hexing Li,Kangnian Fan

DOI: https://doi.org/10.1039/b310316a

IF: 4.9

2003-01-01

Chemical Communications

Abstract:Novel Ag-SiO2-MgO-Al2O3 catalyst prepared by sol-gel method showed extremely high activity and selectivity (both equal to 100%) in the direct dehydrogenation of methanol to anhydrous formaldehyde.
Novel Flower‐Like Ag‐SiO2‐MgO‐Al2O3 Material: Preparation, Characterization and Catalytic Application in Methanol Dehydrogenation

Li Jing-Xia,Fan Kang-Nian,Ren Li-Ping,Dai Wei-Lin,Cao Yong

DOI: https://doi.org/10.1002/cjoc.200890186

IF: 5.56

2008-01-01

Chinese Journal of Chemistry

Abstract:Catalytic direct dehydrogenation of methanol to formaldehyde was carried out over Ag-SiO2-MgO-Al2O3 catalysts prepared by sol-gel method. The optimal preparation mass fractions were determined as 8.3% MgO, 16.5% Al2O3 and 20% silver loading. Using this optimum catalyst, excellent activity and selectivity were obtained. The conversion of methanol and the selectivity to formaldehyde both reached 100%, which were much higher than other previously reported silver supported catalysts. Based on combined characterizations, such as X-ray diffraction (XRD), scanning electronic microscopy (SEM), diffuse reflectance ultraviolet-visible spectroscopy (UV-Vis, DRS), nitrogen adsorption at low temperature, temperature programmed desorption of ammonia (NH3-TPD), desorption of CO2 (CO2-TPD), etc., the correlation of the catalytic performance to the structural properties of the Ag-SiO2MgO-Al2O3 catalyst was discussed in detail. This perfect catalytic performance in the direct dehydrogenation of methanol to formaldehyde without any side-products is attributed to its unique flower-like structure with a surface area less than 1 m(2)/g, and the strong interactions between neutralized support and the nano-sized Ag particles as active centers.
The Oxidative Dehydrogenation of Methanol over a Novel Ag/SiO2 Catalyst

Yong Cao,Wei-Lin Dai,Jing-Fa Deng

DOI: https://doi.org/10.1016/s0926-860x(97)00090-2

IF: 5.723

1997-01-01

Applied Catalysis A General

Abstract:Catalytic oxidative dehydrogenation of methanol to formaldehyde was carried out over a novel Ag/SiO2 catalyst prepared by the sol-gel method. The yield of formaldehyde over this catalyst was ∼10% higher than that over conventional pumice-supported silver and even ∼1% higher than that over commercial electrolytic silver. When the yields were compared under the optimum conditions, the catalytic activity was measured at 820–920 K, O2/CH3OH molar ratio of 0.35–0.55 and at the space velocity of 1.2×105h−1. The thermal behavior and structure of the catalyst were characterized by TG-DTG, DTA and XRD. It was found that this catalyst was thermally stable and silver was present in a crystalline state. SEM was used to determine its morphology and particle size. The silver particle size range was found to be 200–700 nm. XPS results indicated that two different kinds of silver in aggregated and highly dispersed metallic states, were present on the surface of the catalyst.
Ag–SiO2–Al2O3 Composite As Highly Active Catalyst for the Formation of Formaldehyde from the Partial Oxidation of Methanol

WL Dai,C Yong,LP Ren,XL Yang,JH Xu,HX Li,HY He,KN Fan

DOI: https://doi.org/10.1016/j.jcat.2004.08.035

IF: 7.3

2004-01-01

Journal of Catalysis

Abstract:Catalytic oxidative dehydrogenation of methanol to formaldehyde was carried out over Ag-SiO2-Al2O3 catalysts prepared by a sol-gel method. Detailed preparation conditions were investigated and the optimal preparation parameters were determined as the Si/Al molar ratio of 8.5/1.5-9/1, silver loading of 20 wt%, and calcination temperature of 900-1000 degreesC with ethanol as the solvent. Under optimum reaction conditions, i.e., the reaction temperature of 640 degreesC, O-2/CH3OH molar ratio of 0.39 with space velocity (GHSV) of 1.2 x 10(5) h(-1), the as-prepared catalyst exhibits excellent activity and selectivity. The yield of formaldehyde reaches 91%, much higher than that obtained over the pumice-supported silver catalyst (75%) and even higher than that over the commercial electrolytic silver catalyst (85%). Based on combined characterizations, such as X-ray photoelectron spectroscopy and X-ray-excited Auger electron spectroscopy (XPS and XAES), nitrogen adsorption at low temperature, thermogravimetry and differential thermogravimetry (TG-DTG), differential thermal analysis (DTA), diffuse reflectance ultraviolet visible spectroscopy (UV-vis DRS), temperature-programmed reduction (TPR), scanning electron micrograph (SEM), X-ray diffraction (XRD), etc., the correlation of the catalytic performance to the structural properties of the Ag-SiO2-Al2O3 catalyst is discussed in detail. It is found that almost all the catalysts are glass-like and nonporous with a surface area of similar to 1 m(2)/g. In the catalysts with silver loading lower than 20 wt%, all the silver species are present as Ag+ ions before the reaction and the catalyst is ultrathermally stable even under elevated temperatures at 1100 degreesC owing to the stabilizing effect of the [AlO4] group. Higher Ag loading in the catalysts leads to the presence of metallic silver species over the surface of the catalyst. During the catalytic reaction, Ag+ ions are partially reduced to metallic Ag. These nano-sized Ag particles act as the active centers and the superior catalytic performance of the Ag-SiO2-Al2O3 catalyst is attributed to its unique surface structure and the strong interactions between the support and the active phase. (C) 2004 Elsevier Inc. All rights reserved.
The oxidative dehydrogenation of methanol over a novel low‐loading Ag/SiO 2 –TiO 2 catalyst

Qin Liu,Yong Cao,Wei‐Lin Dai,Jing‐Fa Deng

DOI: https://doi.org/10.1023/A:1019010307377

IF: 2.936

1998-01-01

Catalysis Letters

Abstract:Catalytic oxidation of methanol to formaldehyde was carried out over Ag/TiO 2 -SiO 2 catalysts prepared by chemical reduction. The catalytic activity was measured at the temperature interval 820-920 K, O 2 /CH 3 OH molar ratio between 0.35 and 0.50 and at the space velocity of 1.2 × 10 5 h -1 . The optimal content of silver determined by chemical analysis was about 1.7 wt%. The yield of formaldehyde over this catalyst was ~13% higher than that of the industrial pumice-supported silver catalyst and even ~3.5% higher than that of electrolytic silver. The XRD patterns for silver particles supported on TiO 2 -SiO 2 are corresponding to Ag(111), (200) and (220), respectively. SEM was used to determine its morphology and particle size. Isolated silver particles were observed on the surface of the catalyst. O 2 chemisorption by using the pulse technique was carried out to determine the free silver surface areas. The average silver particle size from the calculation of selective oxygen chemisorption was found to be in good agreement with that observed from SEM.
Direct Ink Writing of Hierarchical Porous SiC Ceramics As Catalyst Support for Hydrogen Production

Senyu Qian,Haiyu Liu,Deqing Mei,Yancheng Wang

DOI: https://doi.org/10.1016/j.ceramint.2023.12.191

IF: 5.532

2024-01-01

Ceramics International

Abstract:Due to the tunable porosity at multiple scales, hierarchical porous ceramics feature large specific surface area and excellent heat and mass transfer performance, which can effectively improve the catalytic reaction performance. This paper presents a method to fabricate SiC scaffolds with regular and hierarchical pore structures by direct ink writing (DIW) combined with sacrificial template technology, which can be used as methanol steam reforming (MSR) microreactor catalyst supports. Through printing along a defined path, primary pores with a regular pore structure were created. After sintering, the sacrificial template was removed and secondary pores appeared. Four different types of hierarchical porous SiC scaffolds were successfully prepared and the pore structure, total porosity, linear shrinkage and compressive strength of these scaffolds were investigated. The catalyst coating was then loaded onto the scaffold, and the microstructure characterization showed that the pore structure would not be damaged and blocked. Finally, the hydrogen production experiments were carried out on the MSR microreactor, and the results showed that the support with larger and denser secondary pores had the best fluid flow and hydrogen production characteristics. At the temperature of 280 degrees C and the gas hourly space velocity (GHSV) of 30000 ml g-1 h-1, the methanol conversion and hydrogen production of the best support can reach 90.95 % and 44.96 ml/min, respectively.
Novel highly active Ag–SiO2–Al2O3–ZnO catalyst for the production of anhydrous HCHO from direct dehydrogenation of CH3OH

Li-Ping Ren,Wei-Lin Dai,Xin-Li Yang,Yong Cao,Hexing Li,Kang-Nian Fan

DOI: https://doi.org/10.1016/j.apcata.2004.06.015

2004-01-01

Abstract:A novel four-component Ag–SiO2–Al2O3–ZnO catalyst prepared by sol–gel method shows an outstanding catalytic activity (99% conversion and 87% selectivity) during the process of the direct dehydrogenation of methanol to anhydrous formaldehyde (HCHO). The optimal preparation conditions were found to be 20wt.% loading of silver and zinc content of 15%. The catalytic activity was measured in the temperature range 450–700°C and at the space velocity of 1 × 104h−1, while the optimum reaction temperature was determined to be 650°C. The catalyst was characterized by several kinds of methods: BET method of nitrogen adsorption at −196°C, TG–DTG, SEM, XRD, and NH3-TPD. The catalysts were white powder-like materials and that the BET surface area was ∼0.5m2g−1. All silver was present in an ionic state in the framework of the SiO2–Al2O3–ZnO carrier before catalytic reaction and was thermally stable up to 1000°C. After the reaction, silver was present in the crystalline metal state. The particles were smaller than those found on Ag–SiO2–Al2O3 catalyst.
Ag/MCM-41 As a Highly Efficient Mesostructured Catalyst for the Chemoselective Synthesis of Methyl Glycolate and Ethylene Glycol

Anyuan Yin,Chao Wen,Wei-Lin Dai,Kangnian Fan

DOI: https://doi.org/10.1016/j.apcatb.2011.08.013

2011-01-01

Abstract:A novel highly efficient heterogeneous Ag/MCM-41 catalyst was prepared by ammonia-evaporation deposition-precipitation method and displayed outstanding methyl glycolate (MG) selectivity (up to 99%) and ethylene glycol (EG) selectivity (up to 99%) in the chemoselective gas-phase hydrogenation of dimethyloxalate (DMO). Systematic characterizations have been carried out to elucidate the bulk and surface physicochemical properties of the catalysts. It is shown that the silver loading, the calcination temperature, the surface hydroxyl group amount and the pretreatment atmosphere all have great influences on the catalytic performance of DMO hydrogenation reaction. The best catalytic performance could be achieved over the Ag/MCM-41 catalyst with 10wt.% silver loading after calcined at 673K. Much higher catalytic activity could be obtained via the MCM-41 supported silver catalyst with large amount of surface hydroxyl groups. The argon pretreated Ag/MCM-41 catalyst with less subsurface oxygen species exhibited much higher DMO conversion and MG selectivity compared with H2 and air pretreated samples. Under the optimized reaction conditions, 99% yield of MG and EG could be obtained over the optimized Ag/MCM-41 catalyst.
Dehydrogenation of Alcohols: Formaldehyde

Weilin Dai,Liping Ren

DOI: https://doi.org/10.1002/9783527610044.hetcat0165

2008-01-01

Abstract:AbstractThe sections in this article areIntroductionDirect Dehydrogenation of Methanol to FormaldehydeSilver‐Containing CatalystsCopper‐Containing CatalystsZinc‐Containing CatalystsOther CatalystsIndustrial Applications
Oxidative Dehydrogenation of Methanol to Formaldehyde on Electrolytic Silver Catalyst Modified with Iodides

WL Dai,Q Liu,Y Cao,JF Deng

DOI: https://doi.org/10.1016/s0926-860x(98)00203-8

1998-01-01

Abstract:Iodides, especially CH3I, were used as modifiers in the oxidative dehydrogenation of methanol to formaldehyde over electrolytic silver catalyst. The yield of formaldehyde was as high as 93% at 98% conversion of CH3OH for the I-modified catalyst, while it was only 85% at 94% conversion without I-modification. The optimum reaction conditions were determined and the interaction between the silver surface and the iodide additive was investigated by means of XPS and SEM. The chemisorbed iodine atoms on the silver surface caused a decrease of the surface concentration of atomic oxygen species and prevented the complete oxidation of CH3OH to CO2.
Preparation of silica-supported late transition metal catalyst and ethylene polymerization

Zhi Ma,Wen-Hua Sun,Ning Zhu,Zilong Li,Changxing Shao,Youliang Hu

DOI: https://doi.org/10.1002/pi.853

IF: 3.213

2002-01-01

Polymer International

Abstract:The late transition metal catalyst 2,6-bis[1-(2,6-diisopropylphenylimino)ethyllpyridine iron(II) chloride was supported on silica. Fourier transform infrared spectroscopy, scanning electronic micrograph and X-ray photoelectron spectroscopy measurements were utilized to examine the process of supporting catalyst on silica and investigate the possible mechanism of support. Furthermore, ethylene polymerizations with the supported catalysts were carried out in various conditions such as different reaction temperatures and Al/Fe molar ratios. The results showed that MAO first reacted with the hydroxyl of silica forming Si-O-Al bonds and then the catalyst was bridged through MAO on the surface of silica. Compared with homogeneous catalysts, the supported catalysts show some decrease in catalyst activity. However, they can show good activity at a lower Al/Fe molar ratio with MAO as co-catalyst and give rise to higher molecular weight and melting temperature of the polymer. Better morphology of polyethylene was obtained by a supported catalyst than by its corresponding homogeneous catalyst. (C), 2002 Society of Chemical Industry.

Direct Dehydrogenation of Methanol to Formaldehyde over Novel Ag-Containing Ceramics

A new silver-containing ceramics for catalytic oxidation of methanol to formaldehyde

Direct Dehydrogenation of Methanol to Formaldehyde over Pre-Treated Polycrystalline Silver Catalyst

First Observation of Highly Efficient Dehydrogenation of Methanol to Anhydrous Formaldehyde over Novel Ag–SiO2–MgO–Al2O3catalyst

Novel Highly Active Ag–SiO 2 –MgO Catalysts Used for Direct Dehydrogenation of Methanol to Anhydrous Formaldehyde

Highly active Ag-SiO2-Al2O3 catalyst used for the dehydrogenation of methanol to anhydrous formaldehyde

First observation of highly efficient dehydrogenation of methanol to anhydrous formaldehyde over novel Ag-SiO2-MgO-Al2O 3 catalyst

Novel Sol–gel‐derived Ag/SiO2–Al2O3 Catalysts for Highly Selective Oxidation of Methanol to Formaldehyde

Novel sol–gel‐derived Ag/SiO 2 –Al 2 O 3 catalysts for highly selective oxidation of methanol to formaldehyde

A Novel Silver-Silica Catalyst Used for the Manufacture of Formaldehyde

First observation of highly efficient dehydrogenation of methanol to anhydrous formaldehyde over novel Ag?SiO2?MgO?Al2O3 catalystElectronic supplementary information (ESI) available: XRD and SEM. See http://www.rsc.org/suppdata/cc/b3/b310316a/

Novel Flower‐Like Ag‐SiO2‐MgO‐Al2O3 Material: Preparation, Characterization and Catalytic Application in Methanol Dehydrogenation

The Oxidative Dehydrogenation of Methanol over a Novel Ag/SiO2 Catalyst

Ag–SiO2–Al2O3 Composite As Highly Active Catalyst for the Formation of Formaldehyde from the Partial Oxidation of Methanol

The oxidative dehydrogenation of methanol over a novel low‐loading Ag/SiO 2 –TiO 2 catalyst

Direct Ink Writing of Hierarchical Porous SiC Ceramics As Catalyst Support for Hydrogen Production

Novel highly active Ag–SiO2–Al2O3–ZnO catalyst for the production of anhydrous HCHO from direct dehydrogenation of CH3OH

Ag/MCM-41 As a Highly Efficient Mesostructured Catalyst for the Chemoselective Synthesis of Methyl Glycolate and Ethylene Glycol

Dehydrogenation of Alcohols: Formaldehyde

Oxidative Dehydrogenation of Methanol to Formaldehyde on Electrolytic Silver Catalyst Modified with Iodides

Preparation of silica-supported late transition metal catalyst and ethylene polymerization