Abstract:Catalytic oxidative dehydrogenation of methanol to formaldehyde was carried out over Ag-SiO2-Al2O3 catalysts prepared by a sol-gel method. Detailed preparation conditions were investigated and the optimal preparation parameters were determined as the Si/Al molar ratio of 8.5/1.5-9/1, silver loading of 20 wt%, and calcination temperature of 900-1000 degreesC with ethanol as the solvent. Under optimum reaction conditions, i.e., the reaction temperature of 640 degreesC, O-2/CH3OH molar ratio of 0.39 with space velocity (GHSV) of 1.2 x 10(5) h(-1), the as-prepared catalyst exhibits excellent activity and selectivity. The yield of formaldehyde reaches 91%, much higher than that obtained over the pumice-supported silver catalyst (75%) and even higher than that over the commercial electrolytic silver catalyst (85%). Based on combined characterizations, such as X-ray photoelectron spectroscopy and X-ray-excited Auger electron spectroscopy (XPS and XAES), nitrogen adsorption at low temperature, thermogravimetry and differential thermogravimetry (TG-DTG), differential thermal analysis (DTA), diffuse reflectance ultraviolet visible spectroscopy (UV-vis DRS), temperature-programmed reduction (TPR), scanning electron micrograph (SEM), X-ray diffraction (XRD), etc., the correlation of the catalytic performance to the structural properties of the Ag-SiO2-Al2O3 catalyst is discussed in detail. It is found that almost all the catalysts are glass-like and nonporous with a surface area of similar to 1 m(2)/g. In the catalysts with silver loading lower than 20 wt%, all the silver species are present as Ag+ ions before the reaction and the catalyst is ultrathermally stable even under elevated temperatures at 1100 degreesC owing to the stabilizing effect of the [AlO4] group. Higher Ag loading in the catalysts leads to the presence of metallic silver species over the surface of the catalyst. During the catalytic reaction, Ag+ ions are partially reduced to metallic Ag. These nano-sized Ag particles act as the active centers and the superior catalytic performance of the Ag-SiO2-Al2O3 catalyst is attributed to its unique surface structure and the strong interactions between the support and the active phase. (C) 2004 Elsevier Inc. All rights reserved.

Novel highly active Ag–SiO2–Al2O3–ZnO catalyst for the production of anhydrous HCHO from direct dehydrogenation of CH3OH

Highly active Ag-SiO2-Al2O3 catalyst used for the dehydrogenation of methanol to anhydrous formaldehyde

Novel Highly Active Ag–SiO 2 –MgO Catalysts Used for Direct Dehydrogenation of Methanol to Anhydrous Formaldehyde

Ag–SiO2–Al2O3 Composite As Highly Active Catalyst for the Formation of Formaldehyde from the Partial Oxidation of Methanol

Novel Sol–gel‐derived Ag/SiO2–Al2O3 Catalysts for Highly Selective Oxidation of Methanol to Formaldehyde

Novel sol–gel‐derived Ag/SiO 2 –Al 2 O 3 catalysts for highly selective oxidation of methanol to formaldehyde

Novel Flower‐Like Ag‐SiO2‐MgO‐Al2O3 Material: Preparation, Characterization and Catalytic Application in Methanol Dehydrogenation

First Observation of Highly Efficient Dehydrogenation of Methanol to Anhydrous Formaldehyde over Novel Ag–SiO2–MgO–Al2O3catalyst

The Oxidative Dehydrogenation of Methanol over a Novel Ag/SiO2 Catalyst

First observation of highly efficient dehydrogenation of methanol to anhydrous formaldehyde over novel Ag?SiO2?MgO?Al2O3 catalystElectronic supplementary information (ESI) available: XRD and SEM. See http://www.rsc.org/suppdata/cc/b3/b310316a/

Highly Efficient Hydrogen Production from Formaldehyde over Ag/γ-Al2O3 Catalyst at Room Temperature

First observation of highly efficient dehydrogenation of methanol to anhydrous formaldehyde over novel Ag-SiO2-MgO-Al2O 3 catalyst

Multifunctional Pt/ZSM-5 Catalyst for Complete Oxidation of Gaseous Formaldehyde at Ambient Temperature

Mn-promoted Ag Supported on Pure Siliceous Beta Zeolite (Ag/beta-Si) for Catalytic Combustion of Formaldehyde

The oxidative dehydrogenation of methanol over a novel low‐loading Ag/SiO 2 –TiO 2 catalyst

A Novel Silver-Silica Catalyst Used for the Manufacture of Formaldehyde

Hydroxyl Groups Promoted Ag Dispersion and Excellent Performance of Ag/Al2O3 Catalyst for HCHO Oxidation

Nano-sized Gold Particles Dispersed on HZSM-5 and SiO2 Substrates for Catalytic Oxidation of HCHO

Mesoporous Ag-K-Al 2 O 3 catalysts prepared via a one-pot evaporation induced self-assembly approach and their application in catalytic oxidation of formaldehyde

Synergically regulated silver species and surface oxygen on manganese oxide for promoted activity of formaldehyde oxidation

Direct Dehydrogenation of Methanol to Formaldehyde over Pre-Treated Polycrystalline Silver Catalyst