Melt-Crystallization and Thermal Decomposition Behaviors of Poly(Vinyl Alcohol) Modified by Vinyl Ester with Long Chain

宋兴,陈宁,王琪

DOI: https://doi.org/10.16865/j.cnki.1000-7555.2013.07.017

2013-01-01

Abstract:In this paper,poly(vinyl alcohol)(PVA) with good physical and mechanical properties as well as good thermal processing properties was prepared by copolymerization of vinyl acetate(VAc) and vinyl ester with long chain(Va) and saponification reaction.The effect of Va content on the melt-crystallization and thermal decomposition behaviors of modified PVA was studied by differential scanning calorimetry(DSC) and thermogravimetric analyzer(TG).The results show that the melting temperature of the modified PVA decreases with the content of Va increasing because the formed long branch chain along the PVA molecules can decrease the structure regularity of PVA and increase its intermolecular distance.The decomposition temperature increases with the content of Va increasing due to its shielding effect on the removal of the adjacent hydroxyl groups in the PVA molecules chain.When the molar fraction of Va is 4%,the difference between Tm and Td of modified PVA is up to 92.8 ℃,a wide thermal processing window is got,thus the modified PVA can be thermally processed without any plasticizer,and the tensile strength can reach 64.3MPa.