Synthesis and characterization of organosilicon functionalized water-based polyvinylidene chloride emulsion with core-shell structure
Mengsong Liu,Jiawei Li,Chengyu Hong,Yongquan Wang,Yutong Song,Jiaqi Zhang,Ruixue Zhai,Chao Zhou
DOI: https://doi.org/10.1016/j.mtcomm.2024.108548
IF: 3.8
2024-03-07
Materials Today Communications
Abstract:The outstanding barrier performance of polyvinylidene chloride (PVDC) has attracted widespread attention. In this work, a series of organosilicon functionalized water-based PVDC emulsions with core-shell structure are synthesized by seed emulsion polymerization using vinylidene chloride (VDC), methyl acrylate (MA), isooctyl acrylate (EHA) as core and vinylidene chloride (VDC), methyl acrylate (MA) as shell. Vinyl-terminated polydimethylsiloxanes (VT-PDMS) are introduced into the core-shell as modifier. The properties of PVDC emulsions and films modified with VT-PDMS are investigated. On the one hand, when VT-PDMS is properly incorporated into the core-shell particles, the Si-O bonds in VT-PDMS are dissociated, which further forms a cross-networking structure, thereby enhances the adhesion of PVDC film to the substrate. The barrier performance of the film is also improved by a small amount of cross network structure. On the other hand, the addition of VT-PDMS leads to the phenomenon of thin film shrinkage, which further enhances the barrier performance of PVDC. All results indicate that the best comprehensive performance is achieved when the VT-PDMS content in the PVDC core is 2 wt%, the adhesion can be increased to 0.527 MPa, the oxygen transmittance is 5.68 cc/m 2 ·24 hr, and the actual time of water barrier after coating starch-based tableware is over 12 hours. This provides an effective line of thinking for the further application of PVDC barrier film in the field of environmental protection food packaging.
materials science, multidisciplinary