EFFECT OF HIGH MOLECULAR WEIGHT PVA ON MECHANICAL PROPERTIES OF ICE

Lu Qing,Ma Yuhong,Yang Wantai

DOI: https://doi.org/10.3724/sp.j.1105.2009.01166

2009-01-01

Acta Polymerica Sinica

Abstract:A sample of polyvinyl acetate with M(n) = 1.48 x 10(6) (by GPC) was obtained by bulk photopolymerization, and then it was conversed into poly (vinyl alcohol) with M(eta) = 2.3 x 10(5), as HMWPVA thereafter. The specimens of ice strengthened by HMWPVA were prepared per following procedures: (1) the aqueous solutions of HMWPVA with predetermined concentrations were prepared and then degassed; (2) poured the above solutions in models and then put them in a - 18 degrees C refrigerator for over 48 h. The tensile and compression testing was performed at - 18 degrees C. It showed that with addition of 3 % ( mass fraction) HMWPVA,the values of the tensile strength, elongation at break, compressive strength and compressive modulus of ice were 11.7, 3.5, 2. 3 and 2. 1 times of those of pure ice, respectively. It implied that there was a strong dependence of the tensile strength on the molecular weights of the PVA. Furthermore,the addition of HMWPVA increased the melting time, for example, the melting time of pure ice is about 5 min at 29 degrees C, but the samples with 2 %, 3 % and 4 % HMWPVA are 25 min, 60 min and 240 min, respectively.