Abstract:The purpose of this in vitro study was to evaluate the effect of core ceramic grinding on the fracture behaviour of bilayered lithium disilicate glass-ceramic (LDG) under two loading schemes.Interfacial surfaces of sandblasted LDG disks (A) were ground with 220 (B), 500 (C) and 1200 (D) grit silicon carbide (SiC) sandpapers, respectively. Surface roughness and topographic analysis were performed using a profilometer and a scanning electron microscopy (SEM), and then underwent retesting after veneer firing. Biaxial fracture strength (σf) and Weibull modulus (m) were calculated either with core in tension (subgroup t) or in compression (subgroup c). Failure modes were observed by SEM, and loading induced stress distribution was simulated and analyzed by finite element analysis. Statistical data analysis was performed using Kruskal-Wallis, one-way ANOVA, and paired test at a significance level of 0.05.As the grits size of SiC increased, LDG surface roughness decreased from group A to D (p<0.001), which remained unchanged after veneer firing. No difference in σf (p=0.41 for subgroups At-Dt; p=0.11 for subgroups Ac-Dc), m values as well as failure modes was found among four subgroups for both loading schemes. Specimens in subgroup t showed higher σf (p<0.001) and m values than subgroup c. Stress distribution between loading schemes did not differ from each other. Cracks, as the dominant failure mode initiated from bottom tensile surface. No sign of interfacial cracking or delamination was observed for all groups.Technician grinding changed surface topography of LDG ceramic material, but was not detrimental to the bilayered system strength after veneer application. LDG bilayered system was more sensitive to fracture when loaded with veneer porcelain in tension.Within the limitations of the simulated grinding applied, it is concluded that veneer porcelain can be applied directly after technician grinding of LDG ceramic as it has no detrimental effect on the strength of bilayered structures. The connector areas of LDG fixed dental prosthesis are more sensitive to fracture compared with single crowns, and should be fabricated with more caution.

[Bi-Axial Flexure Strength and Fracture Mode of Alumina Glass-Infiltrated Core/veneer Ceramic Composites].

Biaxial flexural strength of the bilayered disk composed of ceria-stabilized zirconia/alumina nanocomposite (Ce-TZP/A) and veneering porcelain

Weibull analysis and flexural strength of hot-pressed core and veneered ceramic structures

Fracture and Interfacial Delamination Origins of Bilayer Ceramic Composites for Dental Restorations

Effect of Core Ceramic Grinding on Fracture Behaviour of Bilayered Lithium Disilicate Glass–ceramic under Two Loading Schemes

Residual Stress and Reliability of Glass/Alumina Dental Bi-Layer Ceramics

Reliability of flexural strength and subcritical crack growth of dental ceramics

Mechanical properties of commercial high strength ceramic core materials

Flexural strength of glass-infiltrated zirconia/alumina-based ceramics and feldspathic veneering porcelains

Effect of Chemical Strengthening Residual Stress on the Flexural Performance and Fracture Behavior of Aluminosilicate Glass

Role of core support material in veneer failure of brittle layer structures

Quasi-static and Low-Velocity Impact Biaxial Flexural Fracture of Aluminosilicate Glass - an Experimental and Numerical Study

Influence of Ph Value of the Oral Cavity on Biaxial Flexural Strength of Layered Ceramics

Deformation and Failure Behavior of MDYB-3 Oriented PMMA Glass Under Different Loading Conditions

Fracture behavior of lithia disilicate- and leucite-based ceramics

Flexural strengths, failure load, and hardness of glass-ceramics for dental applications

Fracture Behavior of SiC-Whisker-Reinforced Barium Aluminosilicate Glass-Ceramic Matrix Composites

Molecular Dynamics Simulations on Fracture Toughness of Al2O3-SiO2 Glass-Ceramics

A study on thermal compatibility between alumina glass-infiltrated core/vintage AL veneering porcelain

Microstructure and Mechanical Properties of an Alumina–glass Low Temperature Co-Fired Ceramic

[Effect of Core: Dentin Thickness Ratio on the Flexure Strength of IPS Empress II Heat-Pressed All-Ceramic Restorative Material].