Effect of elastic gradients on the fracture resistance of tri-layer restorative systems
Luciano Madeira,Katia R. Weber,Natan Carpenedo,Yu Zhang,Thiago S. Porto,Josete Barbosa Cruz Meira,Carla C. Gonzaga,Marina R. Kaizer
DOI: https://doi.org/10.1016/j.dental.2024.08.004
2024-08-30
Dental Materials Journal
Abstract:Highlights • The biaxial flexural strength of glass-ceramics exceeds that of the hybrid materials. • When bonded to "dentin", the load-bearing capacity is greater for hybrid materials. • When bonded to "dentin", no flexural stress is observed for Lava Ultimate. • Elastic gradients are critical to the fracture resistance of restorative materials. Objectives To assess the impact of elastic gradients formed among restorative material, cement, and substrate on the fracture resistance of tri-layer restorative systems. Methods Four CAD/CAM materials were utilized, two glass-ceramics (IPS e.max CAD, Vita Suprinity) and two resin-ceramic hybrids (Vita Enamic, Lava Ultimate). Their fracture resistance was examined by biaxial flexure ( n = 8) and Hertzian indentation ( n = 10) tests. Statistical analysis was conducted using ANOVA and Tukey tests (p = 5 %). Finite element analysis (FEA) was employed to simulate the Hertzian indentation test and elucidate the stress-fields formed on the intaglio surface below the loading area. Results The biaxial flexural strength (MPa) of glass-ceramics exceeded the hybrid materials (e.max 417 a , Suprinity 230 b , Enamic 138 c , and Lava Ultimate 183 bc ). Conversely, the load-bearing capacity (N) of the materials bonded to dentin analog demonstrated the opposite trend, with the hybrid materials achieving superior results (e.max 830 C , Suprinity 660 D , Enamic 1822 B , and Lava Ultimate 2593 A ). The stress-fields observed by FEA were coherent with the experimental results for Hertzian flexural stresses (MPa): e.max 501 A , Suprinity 342 C , Enamic 406 B , whereas no tensile stress was observed at the intaglio surface of Lava Ultimate. Significance Detailed analysis of the fracture resistance of the tri-layer restorative systems showed that the elastic gradients play a more significant role than the flexural strength of the restorative materials. The coherence of the elastic moduli between the restorative material and supporting structures results in reduced tensile stress concentration at the intaglio surface beneath the loading area and enhances the ability to withstand load.
materials science, biomaterials,dentistry, oral surgery & medicine