Low‐Temperature Sintering Barium Titanate‐Based X8R Ceramics with Nd2O3Dopant and ZnO–B2O3Flux Agent

Changku Sun,Xiaohui Wang,Chao Ma,Longtu Li

DOI: https://doi.org/10.1111/j.1551-2916.2009.03066.x

IF: 4.186

2009-01-01

Journal of the American Ceramic Society

Abstract:To demonstrate that barium titanate‐based ceramics could be sintered at a low temperature thus reducing the cost of capacitor production, systematic investigation has been made on the structure and dielectric properties of barium titanate‐based X8R ceramics, doped with various Nd2O3content and different ZnO–B2O3solution as the sintering aids. The dielectric ceramic powder with good permittivity and low dielectric loss were obtained at a sintering temperature of 900°C, meeting X8R specifications. Transmission electron microscopy and EDS analysis shows a high concentration of Nd element in the boundary regions, which verifies the beneficial role of Nd in facilitating the formation of core‐shell structure. The results also suggest that the developed BaTiO3‐based ceramics may serve as a promising candidate for fabricating cheap multilayer capacitors with pure Ag as inner electrode.