Abstract:In order to study the effect of polycarboxylate superplasticizer (PCE) on the microstructure and strength characteristics of tailings paste, a total of 6 tailings paste combinations including 2 cement-sand ratios (20%, 40%) and 3 water reducer dosages (0, 0.40%, 0.80%) were investigated based on the indoor microstructure test (porosity measurement, XRD test, and SEM observation) and mechanical properties method. The strength of test blocks at different ages was obtained by numerical simulation. The results showed that: 1) The water reducer can effectively reduce the porosity of the tailings paste, and the reduction effect was more significant in the condition of high cement-sand ratios. Meanwhile, high cement-sand ratio is conductive to generate more beneficial hydrates such as portlandite; 2) Compared with the significant effect of cementitious agent on the tensile strength σ t of the paste, the effect of water reducer on σ t is weak. Accordingly, the σ t of the tailings paste is much more sensitive to cementitious agent than water reduce; 3) SEM images show that the better ratio of slurry containing polycarboxylic acid superplasticizer has more C-S-H cementitious content, smaller pore size and shorter molecular chain between particles, indicating that the particles are more encapsulated and the early strength is improved. 4) The incorporation of water reducer enhancement was particularly significant under the condition of triaxial compression. However, the presence of water reducer did not change its deformation characteristics, when the confining pressure is low, the strain softening appears; and when the confining pressure is high, it transforms to strain hardening. The peak strain ε 0 and the confining pressure σ 3 had a linear relationship; 5) The strength of the paste was significantly affected by the confining pressure σ 3 under different conditions. The peak intensity σ 1 and the confining pressure σ 3 satisfied a linear relationship, while the residual strength σ r and the confining pressure σ 3 satisfied a quadratic polynomial fitting relationship. The strength parameters cohesion c and internal friction angle φ were both positively correlated with the water reducer dosage.

Investigations on the Compatibility of Ordinary Cement and Water Reducer by Using Cross-cut Testing

Study on Compatibility of Comb-like Polycarboxylic Acid Type Water-reducer with Cements

Optimization of Formula for Stabilizing Muddy Soil Using Response Surface Methodology

Influence of Superplasticizer Type and Dosage on Early-age Drying Shrinkage of Cement Paste with Consideration of Pore Size Distribution and Water Loss

Research on Sustainable Development of Fine-Grained Material Cement Slurry

Effect of Additives on the Rheological and Mechanical Properties of Microfine-Cement-Based Grout

Development of cementitious capillary crystalline waterproofing agents and durability study of concrete in the presence of chloride with sulfate in aqueous environment

Effects of Water-to-Cement Ratio on Pore Structure Evolution and Strength Development of Cement Slurry Based on HYMOSTRUC3D and Micro-CT

Use of Water Reducer to Enhance the Mechanical and Durability Properties of Cement-Treated Soil

Investigation on the Effects of Shrinkage-Reducing-waterproofing Admixture on Concrete Dry-Shrinkage Property

Experimental Research on the Microstructure and Strength Characteristics of Tailings Paste Containing Wate Reducer

DFT Study on the Compatibility Between Bentonite Clay Mineral and Hydration Products With the Polycarboxylate Water Reducer in the Cement Hydration Process

Study on the rheological properties of Portland cement pastes with polycarboxylate superplasticizers

Research on optimizing performance of desulfurization-gypsum-based composite cementitious materials based on response surface method

Experimental and numerical study on the mitigation of autogenous shrinkage of cementitious material

Study on the Compatibility of Cement-Superplasticizer System Based on the Amount of Free Solution

Investigations on the rehydration of recycled blended SCMs cement

Research on Cement Slurry Using Silica Fume Instead of Fly Ash

Investigation of self-compacting concrete utilizing different supplementary pozzolanic materials for cement replacement

Investigating the sulfate resistance of mortars with multiple mineral admixtures in ammonium-magnesium sulfate solution

New Method to Evaluate Rheological Behavior of High Fluidity Cement Paste and Mortar