Coating effect of Al2O3 on ZnMn2O4 anode surface for lithium-ion batteries
Guangfu Liu,Qing Han,Kuiren Liu
DOI: https://doi.org/10.1007/s11581-024-05646-7
IF: 2.961
2024-06-16
Ionics
Abstract:Zinc manganese oxide (ZnMn 2 O 4 ), exhibiting a clustered spherical structure, is synthesized using a low-temperature coprecipitation method. Following this, a coating of nano-sized Al 2 O 3 is applied via a wet chemical technique. The resultant materials—designated as ZnMn 2 O 4 (ZMO) and Al 2 O 3 —coated ZnMn 2 O 4 (ZMO-AlO)-undergo characterization using X-ray diffraction, scanning electron microscopy, and X-ray photoelectron spectroscopy. Scanning electron microscopy reveals that both ZMO and ZMO-AlO retain their clustered spherical morphologies. Furthermore, XPS and TEM confirm the presence of an Al 2 O 3 layer on the ZMO-AlO sample. In terms of electrochemical performance, a significant improvement is observed. Specifically, the Al 2 O 3 coating enhances the initial discharge capacity of ZMO-AlO to 1228 mAh·g −1 , compared to the 1140 mAh·g −1 capacity of the unmodified ZMO material. During the second charging and discharging cycle, the ZMO-AlO samples demonstrate specific capacities of 763 and 788 mAh·g −1 , respectively, achieving a coulombic efficiency of 96.8%. By contrast, the ZMO samples show specific capacities of 760 and 715 mAh·g −1 , respectively, with a slightly lower coulombic efficiency of 94.1%. When evaluating the electrochemical lithium storage performance of ZMO and ZMO-AlO at a current density of 100 mA·g −1 , it becomes evident that the Al 2 O 3 -modified ZnMn 2 O 4 (ZMO-AlO) offers superior performance compared to the unmodified ZMO.
chemistry, physical,physics, condensed matter,electrochemistry