Abstract:SiC layer was prepared in an industrial scale spout fluidized bed by chemical vapor deposition. The density of SiC coating was about 3.18 g/cm(3). High temperature oxidation experiments were carried out at different temperatures from 800 to 1600 degrees C. The microstructure and composition were characterized using different methods, including mass change weighing, XRD, EDS and SEM. It was found that the weight gain of SiC coating layer was not obvious below 1200 degrees C, and subsequent mass gain gradually increased with increasing temperature, reaching 10% at 1600 degrees C. High-magnification SEM results show that the oxidation began from the surface and gradually formed punctate distribution of the oxide. Small crystal structure (similar to micron) of the SiC surface was very clear at 1000 degrees C, and this crystal structure disappeared gradually at high temperatures, forming oxides of Si in the SiC surface. There was a stacking fault stress due to the different thermal expansion coefficients and elastic modulus of SiC and Si oxides, leading to the gradual formation of cracks around the punctates. With increasing temperature, the crack further increased the oxidation rate of SiC, and finally the formed Si oxides layer fell off from the particles. It can be seen clearly that the layer was peeling when the temperature was increased to 1400 degrees C. Increasing the temperature to 1600 degrees C, the SiC coating was oxidized completely into a honeycomb structure, with obvious sintering of SiC. XRD analysis shows that there was a growing SiO2 peaks from 1400 degrees C, indicating that surface oxidation was significant. EDS results shows that the oxygen content in the coating surface gradually increased with increasing temperature. Semi-quantitative analysis shows that the surface was close to SiO2 at 1600 degrees C.

Oxidation behavior of oxidation protective coatings for C/C-SiC composites at 1500 ℃

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

Oxidation Protection of C/C Composites with a Multilayer Coating of SiC and Si + SiC + SiC Nanowires

Microstructure And Oxidation Resistance Of Carbon/Carbon Composites Coated With Si3n4-Si/Mosi2-Sic Multi-Layers By Slurry Coating And Post Heat-Treatment Process

A Multilayer MoSi2–SiC–B Coating to Protect SiC-coated Carbon/carbon Composites Against Oxidation

Oxidation Protection of C/C Composites by Ultra Long SiC Nanowire-Reinforced SiC–Si Coating

SiC_n/SiC Multilayer Oxidation Protective Coatings for C/C Composites Prepared by a Hydrothermal Electrophoretic Deposition Process

Microstructure and Oxidation Resistant Property of C/C Composites Modified by SiC–MoSi2–CrSi2 Coating

Fabrication and oxidation resistance of mullite/yttrium silicate multilayer coatings on C/SiC composites

SiC Nanowire-Toughened SiC–MoSi2–CrSi2 Oxidation Protective Coating for Carbon/carbon Composites

Oxidation protection and behavior of C/C composites with an in situ SiC nanowire-SiC-Si/SiC-Si coating

A ZrB2–SiC/SiC Oxidation Protective Dual-Layer Coating for Carbon/carbon Composites

Comparison of Oxidation Behaviors of 3D C/PyC/SiC and SiC/PyC/SiC Composites in an O2-Ar Atmosphere

A Thick SiC-Si Coating Prepared by One-Step Pack Cementation for Long-Term Protection of Carbon/carbon Composites Against Oxidation at 1773 K

Effect of heat-treatment on the oxidation resistance of Mo-Si-N coating for C/C composites

High Temperature Oxidation Behavior of SiC Coating Materials

A dense ZrB2-SiC-Si/SiC-Si coating to protect carbon/carbon composites against oxidation at 1773 K and 1973 K

Improved antioxidative and mechanical properties of SiC coated C/C composites via a SiO2-SiC reticulated layer

Deposition voltages on the phase evolutions, microstructures, and oxidation behaviors of thermal-resistance Glass-MoSi2-SiC coating

Effect of Mo/Si Ratio on the Microstructure and Oxidation Resistance of Si-Mo Coating for C/C Composites

Siliconization elimination for SiC coated C/C composites by a pyrolytic carbon coating and the consequent improvement of the mechanical property and oxidation resistances