A reactive extrusion process for the synthesis of polyamide graft copolymers
Guo-Hua Hu,Cai-Liang Zhang,Lian-Fang Feng,Sandrine Hoppe
2007-01-01
Abstract:This work further studies a previous approach to synthesize graft copolymers with polystyrene (PS) as the backbone and polyamide 6 (PA6) as the grafts. The underlying chemistry is the use of a random copolymer of styrene and 3-isopropenyl-α, α-dimethylbenzene isocyanate (TMI), PS-co-TMI, to activate the polymerisation of ε-caprolactam (CL) in the presence of sodium ε-caprolactam (NaCL) as an anionic catalyst. The composition of the resulting material and the effects of various parameters on the polymerisation kinetics were studied. Results showed that all isocyanate moieties of the PS-co-TMI participated in the activation of the polymerisation. Moreover, to obtain sufficiently high reaction rate and monomer conversion, the following conditions should be met simultaneously: polymerisation temperature higher than 220 oC, TMI content in PS-co-TMI higher than 2% and the molar ratio between the isocyanate group in PS-g-TMI and NaCL smaller than 3.4. Feeding mode had a little effect on the CL conversion but had a strong effect on the induction time of polymerisation. Introduction The concept and practice of compounding two or more polymers to obtain new polymer materials having high performance have received much attention from the point of view of fundamental and practical interest during the last three, up to four decades. However, the majority of polymer blends are immiscible and most of them possess high interfacial tension and weak adhesion at the interfaces between the matrix and the dispersed phase, forming very coarse morphology due to macrophase separation. As a result, some of their properties can be much worse than those of each of the blend components. A compatibiliser is therefore required [1]. Block or graft copolymer is often used as compatibiliser to reduce the size of dispersed phase, enhance the adhesion between the phases and stabilize the dispersed phase [2, 3]. It may also accelerate the melting process of polymer blends [4], a critical step for melt polymer blending [5, 6]. Many chemical routes cannot be followed easily or in an economically feasible fashion to synthesize block or graft copolymers for industrial compatibilisation purposes. One that has been frequently practiced consists of reacting two mutually reactive polymers. However, this method hardly leads to the formation of pure copolymers when the reactive polymers are immiscible, unless the chain length of at least one of them is relatively short [7], or once formed at the interfaces the copolymer chains walk away. Limited amounts of copolymer formed by interfacial reactions are due to limited amounts of interfacial volume that are available for reaction between two immisicible polymers, even under intense mixing [8, 9]. Some 30 years ago, Matzner et al. [10, 11] reported on a chemical route for the synthesis of graft copolymers with polystyrene (PS) or polyethylene as the backbone and polyamide 6 (PA6) as grafts. It was based on the use of acrylic esters incorporated in polystyrene or polyethylene as activators from which the polymerisation of ε-caprolactam (CL) began could grow in the presence of an anionic catalyst such as sodium ε-caprolactam (NaCL), leading to the formation of PA6 grafts. Ester and bischloroformate bearing polymers were also used to activate the polymerisation of CL to form graft copolymers [12, 13]. However, the activation performance of those types of activators is relatively low. Therefore, the time necessary for the polymerisation to go to completion is very long compared to the mean residence time of a typical reactive extrusion process, which is often much less than a few minutes. Hu et al. [14-18] used isocyanatebearing polypropylene as activators. The latter showed a much higher activation performance. For example, high purity graft copolymers of polypropylene (PP) and PA6, were obtained in a about a minute in a batch mixer when CL was polymerised onto a 3-isopropenyl-α, α-dimethylbenzene isocyanate (TMI) that was grafted onto PP (PP-g-TMI). NaCL was used as the catalyst of the polymerisation. However, previous studies [14-18] on the anionic polymerisation of CL onto PP-g-TMI did not answer the following two key questions. First, did all the isocyanate moieties participate in the activation of the polymerisation of CL? In other words, were there any isocyanate-bearing polymer chains that remained intact at all at the end of the polymerisation? Second, CL and PP-g-TMI were immiscible. Would the polymerisation conditions recommended for such immiscible systems still be suitable for other similar but miscible ones? To address these two questions, in this work a random copolymer of styrene and 3-isopropenyl-α, α-dimethylbenzene isocyanate (TMI), PS-co-TMI, was used