Abstract:Silicon carbide nanostructures were synthesized by carbothermal reduction of carbon-silica (C-SiO2) nanocomposites. C-SiO2 nanocomposites with C/SiO2 molar ratios of 1.90-4.21 were used in this study. Thermogravimetric analysis, nitrogen sorption, X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and infrared spectroscopy were used to characterize C-SiO2 nanocomposites and SiC products. Highly crystalline SiC nanoparticles and nanofibers (CS-3.28 and CS-4.21) were obtained from mesoporous C-SiO2 nanocomposites with the carbon content greater than a C/SiO2 stoichiometric ratio of 3 (e.g., C/SiO2 = 3.28 and 4.21 by mole), and they had a BET surface area of 83.0-76.7 m(2)/g after unreacted silica and carbon were removed. In contrast, SiC was not formed in the mesoporous C-SiO2 nanocomposites with a lower carbon content (e.g., C/SiO2 = 1.91 and 2.51 by mole). However, when such mesoporous nanocomposites were infiltrated with a small amount of carbon, SiC nanoparticles and nanofibers with high crystallinity were produced. The major phase formed from the mesoporous C-SiO2 nanocomposite with C/SiO2 = 2.51 was nanofibers, and only less than 15% nanoparticles was observed in this sample. The carbothermal reduction of dense C-SiO2 nanocomposites resulted in mesoporous SiC with low crystallinity under the heating conditions used. As a result, the pores play a vital role in the carbothermal reduction of C-SiO2 nanocomposites. SiC with controlled nanostructures can be synthesized by simply varying the porosity, C/SiO2 ratio, and structure of the precursors.

Role of Pores in the Carbothermal Reduction of Carbon−Silica Nanocomposites into Silicon Carbide Nanostructures

Synthesis and properties of porous SiN/SiC nanocomposites by carbothermal reaction between SiN and carbon

Microstructure and Mechanical Properties of Porous SiC Ceramics by Carbothermal Reduction and Subsequent Recrystallization Sintering

Porous 2h‐silicon Carbide Ceramics Fabricated by Carbothermal Reaction Between Silicon Nitride and Carbon

Preparation Of Nanocrystalline Silicon Carbide Powders By Carbothermal Reduction

Synthesis of nanocrystalline silicon carbide powders

Carbothermal Reduction Behavior of Micro-silica

Effect of Sintering Conditions on the Formation of SiC Nanomaterials in Carbothermal Reduction

Low-temperature formation of nanocrystalline β-SiC with high surface area and mesoporosity via reaction of mesoporous carbon and silicon powder

Synthesis and Characterization of Si/SiO2/SiC Composites Through Carbothermic Reduction of Rice Husk-based Silica

Porous Silicon Nitride Ceramics Prepared by Carbothermal Reduction Method

Theoretical and experimental study of the mechanism for preparation of SiC nanowires by carbothermal reduction

Preparation and Characterization of SiC Nanowires and Nanoparticles from Filter Paper by Sol–gel and Carbothermal Reduction Processing

Effects of in situ formed nanostructures on the structure and properties of C/SiOC composites

Fabrication and Characterization of Hierarchical Porous SiC Ceramics Via Gelcasting and Carbothermal Reduction Between Carbon and SiO

Synthesis of Silicon Carbide Nanopowder Using Silica Fume

Ordered Mesoporous SiOC and SiCN Ceramics from Atmosphere-Assisted in Situ Transformation

Synthesis of Porous Silicon Nitride Ceramics from Diatomite

Carbothermally prepared nanophase SiC/ Si3N4 composite powders and densified parts

A Novel Method for the Preparation of Porous SiC

Microstructure Evolution and Reaction Mechanism of Microporous Carbon Derived SiC Ceramic