Abstract:Wear test setup. This study investigates the effects of filler content and type on the mechanical (tensile strength and impact resistance) and tribological properties of woven glass fiber‐reinforced composites (WGFC) produced using three different nanofillers (MgO, CuO, and Al2O3) at various loading levels (0.7, 1.4, and 2.8 wt%). Additionally, analyses of the artificial neural network algorithm were reported for the predictions of wear rate, mass loss, and coefficient of friction (COF) by given applied load, sliding distance, filler ratio, and filler type. The composites were fabricated using the hand lay‐up method. The filled composites were characterized using Fourier Transform Infrared (FTIR) spectroscopy, and the worn surfaces of the samples after the wear test were analyzed using Scanning Electron Microscopy (SEM). The wear resistance of the composite samples improved at 0.7 wt% CuO and 1.4 wt% MgO filler contents. At 200 m sliding distance and 1.4 wt% filler ratio, the highest wear ratio was determined as 55 mm3/m × 10−3 in the Al2O3‐filled composite, and the lowest was determined as 31 mm3/m × 10−3 in the MgO‐filled composite. At 1.4% filler ratio and 15 N load, the lowest friction coefficient was determined as 0.45 μ in MgO‐filled composite, and the highest was 0.56 μ in Al2O3‐filled composite. Al2O3 filler increased the mass loss and wear rate of the composite material. In Charpy impact tests, the maximum impact energy of 13.9 J/m2 was obtained with a 2.8 wt% Al2O3 filler content. Tensile tests showed an increase in tensile strength for all filler contents compared to unfilled composites. The highest tensile strength of 242.1 MPa was achieved with 0.7 wt% CuO reinforcement. Highlights In all applied wear parameters and filler ratios, the Al2O3 filler adversely affected the wear resistance of the composite, while the MgO filler showed the best performance in terms of wear resistance. All types and ratios of fillers increased the tensile strength compared to the unfilled composite. Contrary to its negative effect on wear, the Al2O3‐filled composites exhibited the highest impact resistance. The prediction analysis of the tribological behavior of composite material using ANN reveals that the Levenberg–Marquardt algorithm fits very well.

Mechanical Properties and their Influence on the Friction and Wear of Polyamide6 Composites Filled with Nano SiO2 and Glass Fiber

Effect of Lubricating Condition on Tribological Properties of Nano-SiO2 Filled Polyamide Composite

Effect of different fillers on thermal conductivity, tribological properties of Polyamide 6

The mechanical and tribological properties of CF/PPS composite filled with PA6

Microstructural, Mechanical, and Tribological Performances of Composites Prepared via Melt Compounding of Polyamide 6, Basalt Fibers, and Styrene–Ethylene–Butylene–Styrene Copolymer

Mechanical and Tribological Properties of 3D Printed Polyamide 12 and SiC/PA12 Composite by Selective Laser Sintering

Tribological Properties of Glass Bead-Filled Polyamide 12 Composite Manufactured by Selective Laser Sintering

Mechanical and tribological properties of PA66/PPS blend. III. Reinforced with GF

Tribological Properties of SiC Particle Filled in Monomer Cast Nylon

Mechanically Robust and Abrasion-Resistant Polymer Nanocomposites for Potential Applications As Advanced Clearance Joints

Comparative Evaluation of Tribological Effectiveness of Carbon- and Glass-Filled Polyamide Composites Using Submicromechanical Diagnostics of Surface Layers before and after Wear Tests during Dry Sliding Friction

Influence of glass fiber on tribological characteristics and wear mechanism of MC nylon-based composite

Tribological Behavior of Polyamide 66‐based Binary and Ternary Composites

Friction and Wear Performance of PTFE Modification Composites Filled with Micrometer and Nanometer MoS2

Application of Submicromechanical Diagnostics for Characterization of Glass-Filled Polyamide Composites

Mechanical and tribological performances of ceramic microsphere reinforced polyamide 6 composites

Mechanical Properties and Friction and Wear Properties of Nano-Al_2O_3 Modified POM Nanocomposites

Tribological and mechanical properties of nanofilled glass fiber reinforced composites and analyzing the tribological behavior using artificial neural networks

Tribological and Mechanochemical Properties of Nanoparticle-Filled Polytetrafluoroethylene Composites under Different Loads

Mechanical and Tribological Performances of Thermoplastic Polymers Reinforced with Glass Fibres at Variable Fibre Volume Fractions

Improvement of mechanical and wear resistance property by varying glass fiber contents and amino-silicate coupling agents on polyamide 612 composites