Abstract:Single‐crystalline TiC nanocubes with exposed {100} facets are grown by combusting a TiO2 + kMg + C reactive mixture in argon. The mechanism of TiC nanocube formation is discussed, and the Wulff shapes of the nanocrystals are constructed. The electrocatalytic performance of the TiC nanocubes is evidenced by a low overpotential of 0.298 V at 10 mA cm−2. Although TiC nanostructures show promise as non‐noble‐metal‐based electrocatalysts, improved synthesis methods are required. Herein, single‐crystalline TiC nanocubes with exposed {100} facets are grown by combusting TiO2 + kMg + C reactive mixtures (k = 4–6.5 mol) in argon. During the synthesis, the temperature increases to 1200–1550 °C and excess Mg (2–4.5 mol) forms a liquid pool. The obtained TiC nanocubes have edge lengths of 50–300 nm and surface areas of 12.2–30.05 m2 g−1. Insights into the TiC nanocube formation mechanism are obtained using density functional theory modeling of the surface energies of TiC nanocrystals and shape visualization using the Wulff construction method. During TiC nucleation and growth within the Mg melt, liquid Mg likely acts as a capping agent for {111} facets, thus promoting the formation of {100} facets. The TiC nanocubes show high electrocatalytic activity for the hydrogen evolution reaction, with a lower overpotential (0.298 V at 10 mA cm−2) than other TiC nanostructures (0.400–0.815 V).

Growth of Trigonal-Shaped Tin Nanocrystals Via the Metal-Catalyzed Reduction-Nitridation Route at Low Temperature

Liquid‐Metal‐Assisted Synthesis of Single‐Crystalline TiC Nanocubes with Exposed {100} Facets for Enhanced Electrocatalytic Activity in the Hydrogen Evolution Reaction

The co-reduction route to TiC nanocrystallites at low temperature

Rapid-Heating-Triggered in Situ Solid-State Transformation of Amorphous TiO2 Nanotubes into Well-Defined Anatase Nanocrystals

Thermal Nitridation Synthesis of MN (m=ti, V and Cr) Nanocrystals from Metals and NH4Cl

A New Reduction-Carburization Route to Nanocrystalline Tic

Preparation of nano-TiN powders by Ni-catalysed carbothermal reduction nitridation

Formation Of Nanocrystalline Tin Film By Ion-Beam-Enhanced Deposition

Low-temperature Synthesis of TiB2 Nanocrystals Using TiO2 ,LiBH4 and Mg

Low-Temperature Synthesis of Nanocrystalline Titanium Nitride via a Benzene-Thermal Route

Low‐Temperature Growth of Monolayer Rutile TiO2 Nanorod Films

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Synthesis of Uniform Titanium Nitride Nanocrystalline Powders Via a Reduction–Hydrogenation–Dehydrogenation–Nitridation Route

Synthesis of Ti(C,N) Powder Via CRN Method from Rutile/Carbon Mixtures

Synthesis and characterization of nanocrystalline TaN

Formation Of Nanocrystalline Tic By A Low-Temperature Route

Formation of TaC Nanorods with a Low-Temperature Chemical Route

Synthesis of Nanocrystalline Titanium Nitride Powders by Direct Nitridation of Titanium Oxide

A Simple Route to Prepare Nanocrystalline Titanium Carbonitride

Preparation of nanocrystalline TiN film by direct nitridation of TiO2 film

Sol-Gel Preparation of N-doped TiO2 Nanocrystalline at Low Temperature