Abstract:In this article, we fabricated ZnO nanorod arrays on ITO substrates by cathodic electrodeposition method under different electrodeposition times. The XRD results illustrate that all of the peaks can be attributed to the hexagonal wurtzite structure. Besides, the crystallinity and the preferred c-axis orientation increase with longer electrodeposition time. With the increasing electrodeposition time, the diameter of nanorods, the surface roughness and thickness of ZnO nanorod arrays also increased. All samples exhibit hydrophobic behavior and the water contact angle (CA) increases to 120 degrees with the electrodeposition time increases to 120 min. After 10 min of ultraviolet (UV) irradiation, the wettability of the ZnO surfaces turn from hydrophobic to hydrophilicity, and the change of the CA reduction rate are 73.5, 63.5, 48.3 and 24.2%, corresponding to the sample electrodeposited 10, 30, 60 and 120 min, respectively. The intensity of UV emission peak ratio increases from 2.26 to 63.84% while the visible emission peak ratio decreases in PL spectra, which reveals defects decrease when electrodeposition time increases from 10 to 120 min. Raman spectrum shows three peaks which are located at 439, 566 and 1097 cm(-1), corresponding to the E-2, E-1L and E-3 mode of ZnO. (C) 2016 The Electrochemical Society. All rights reserved.

Effects of Pretreatment of Substrates on the Preparation of Large Scale Zno Nanotube Arrays

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Effect of UV irradiation on the properties of ZnO nanorod arrays prepared by hydrothermal method

Preparation of Large-Scale Highly Oriented Zno Noodle Arrays and Study on the Photoconductivity

Effect of Substrate Pretreatments on the Growth of SnO_2 Nanowire Arrays by Hydrothermal Method

Effect of Electrodeposition Time on Microstructure, Wettability and Optical Properties of ZnO Nanorod Arrays

Effects of preparing conditions on controllable one-step electrodeposition of ZnO nanotube arrays

Effect of Substrate Pretreatment on Controllable Growth of TiO2 Nanorod Arrays

Effect of Substrate Pre-Treatment on Controllable Synthesis of Hexagonal WO3 Nanorod Arrays and Their Electrochromic Properties

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Density-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Controlling the hydrothermal growth and the properties of ZnO nanorod arrays by pre-treating the seed layer

Substrate effect on Electrodeposition of ZnO nanorod Arrays

One-step electrodeposition of single-crystal ZnO nanotube arrays and their optical properties

Effect of Sapphire Substrate Pre-Treatment on the Growth of Zno Films

Electrochemical/Chemical Synthesis of Highly-Oriented Single-Crystal Zno Nanotube Arrays on Transparent Conductive Substrates

Effects of preparing conditions on the electrodeposition of well-aligned ZnO nanorod arrays

Effect of substrate surface treatment on the hydrothermal synthesis of zinc oxide nanostructures

Synthesis of Zno Nanorods Arrays on Ito and Their Photoelectrochemical Performance

Preparation and Optimization of Vertically Arrayed Zinc Oxide Nanorods

Controllable Preparation and Photocatalytic Activity of Highly Ordered ZnO Nanoarrays