Abstract:Reversible reaction involving Li amide (LiNH$_{2}$) and Li imide (Li$_{2}$NH) is a potential mechanism for hydrogen storage. Recent synchrotron x-ray diffraction experiments [W. I. David et al., J. Am. Chem. Soc. 129, 1594 (2007)] suggest that the transformation between LiNH$_{2}$ and Li$_{2}$NH is a bulk reaction that occurs through non-stoichiometric processes and involves the migration of Li$^{+}$ and H$^{+}$ ions. In order to understand the atomistic mechanisms behind these processes, we carry out comprehensive first-principles studies of native point defects and defect complexes in the two compounds. We find that both LiNH$_{2}$ and Li$_{2}$NH are prone to Frenkel disorder on the Li sublattice. Lithium interstitials and vacancies have low formation energies and are highly mobile, and therefore play an important role in mass transport and ionic conduction. Hydrogen interstitials and vacancies, on the other hand, are responsible for forming and breaking N$-$H bonds, which is essential in the Li amide/imide reaction. Based on the structure, energetics, and migration of hydrogen-, lithium-, and nitrogen-related defects, we propose that LiNH$_{2}$ decomposes into Li$_{2}$NH and NH$_{3}$ according to two competing mechanisms with different activation energies: one mechanism involves the formation of native defects in the interior of the material, the other at the surface. As a result, the prevailing mechanism and hence the effective activation energy for decomposition depend on the surface-to-volume ratio or the specific surface area, which changes with particle size during ball milling. These mechanisms also provide an explanation for the dehydrogenation of LiNH$_{2}$+LiH mixtures.

Interaction Between Lithium Amide and Lithium Hydride

Mechanisms for the decomposition and dehydrogenation of Li amide/imide

Bonding Mechanism and Stability of Lithium Hydrides

An Investigation on the Reaction Pathway Between LiAlH4 and LiNH2 Via Gaseous Ammonia

Thermal-decomposition synthesis and hydrogen desorption behavior of LiBH4 ·NH3

Hydrogen Release from Amminelithium Borohydride, LiBH4 X NH3.

Thermal Dehydrogenation Behaviors and Mechanisms of Mg(BH4)2∙6NH3-xLiH Combination Systems

Hydrogen Desorption Kinetics of the Destabilized LiBH 4 AlH 3 Composites

Large Amount of Hydrogen Desorption from the Mixture of Mg(Nh2)(2) and Lialh4

Behavior of Lithium Amide Under Argon Plasma

Large volume collapse during pressure-induced phase transition in lithium amide

Destabilized dehydrogenation reaction of LiBH4 by AlF 3

In Situ Formation of Lithium Fast-Ion Conductors and Improved Hydrogen Desorption Properties of the LiNH2–MgH2 System with the Addition of Lithium Halides

Improved hydrogen desorption properties of LiBH4 by AlH3 addition

Enhanced reversible hydrogen desorption properties and mechanism of Mg(BH 4 ) 2 -AlH 3 -LiH composite

Dehydrogenation Promotion of LiBH<sub>4</sub>·NH<sub>3</sub>Through Heating in Ammonia or Mixing with Metal Hydrides

Dehydrogenation Promotion of LiBH4·NH3 Through Heating in Ammonia or Mixing with Metal Hydrides

Hydrogen Storage Reaction over A Ternary Imide Li2mg2n3h3

Hydrogen Absorption/desorption Properties of Li–Al–N–H Composite

A Combined Hydrogen Storage System of Mg(BH4)2−LiNH2 with Favorable Dehydrogenation

Dehydrogenation promotion of LiBH4 center dot NH3 through heating in ammonia or mixing with metal hydrides