Growth Rate and Composition of Directionally Solidified Intermetallic TiAl–Nb Alloys with Different Solidification Conditions
Li-Wei Zhang,Jun-Pin Lin,Xiang-Jun Xu,Jian-Ping He,Xian-Fei Ding,Xiao-Ou Jin
DOI: https://doi.org/10.1007/s12598-015-0637-8
IF: 6.318
2015-01-01
Rare Metals
Abstract:Intermetallic Ti-xAl-8Nb（x = 41,43,45,47,49;at%） alloys were solidified unidirectionally upwards with a constant temperature gradient of G=3.8 K·mm -1 at wide range of growth rates of v=10-400 μm·s -1 using a Bridgman directional solidification（DS） furnace.Microstructural parameters including the primary dendrite arm spacing（λ 1 ）,secondary dendrite arm spacing（λ 2 ）,dendrite tip radius（R） and mushy zone depth（d） were measured statistically.The values of λ 1 ,λ 2 ,R and d decrease as the growth rate increases for a given composition（x）.The values of λ 1 ,λ 2 ,R and v increase with the increase in x value,while the value of d firstly increases and then decreases with the increase in x value for a given v.The relationships between λ 1 ,λ 2 and R were analyzed by the linear regression.The average growth rate exponent of λ 1 is 0.29,which is in accordance with the previous experimental observations,and that of λ 2 is close to the previous experimental results,while those of R and d are lower than the results in other alloy systems.In addition,theoretical models for λ 1 ,λ 2 and R were compared with the experimental observations,and a comparison of the present experimental results with the theoretical models and previous experimental results was also made.