Effect of Heating Temperature on Microstructure of Directionally Solidified Ni-45Ti-5Al Alloy

YANG Chunlci,ZHANG Xiaoli,ZHENG Lijing,ZHANG Hu

DOI: https://doi.org/10.3969/j.issn.1001-3814.2011.09.022

2011-01-01

Abstract:The microstructure evolution of Ni-45Ti-5Al(at,%) alloy prepared by directional solidification with liquidmetal-cooling at 1450 ℃,1550 ℃ and 1650 ℃,respectively,was investigated.The results show that the macro-structure in directional solidification growth is columnar grain.The effect of directional solidification is good.The microstructure grows in cellular form,which is composed of primary NiTi matrix and Ti2Ni precipitates.The preferred orientation of NiTi and Ti2Ni is respectively and direction.Aluminum dissolves in both NiTi and Ti2Ni phase.The Al content in the matrix is higher than that in the precipitates.As the heating temperature increasing,the microstructure evolution is inconspicuous and the average cellular interval is 30～50 μm.The precipitation content of Ti2Ni is most when the heating temperature is 1550 ℃.