Structure Evolution of Directionally Solidified Ti-43al-3si Alloy Ii. Microstructure Evolution in the Steady-State Growth Region

Li Xinzhong,Fan Jianglei,Guo Jingjie,Su Yanqing,Fu Hengzhi
DOI: https://doi.org/10.3321/j.issn:0412-1961.2009.03.009
IF: 1.797
2009-01-01
ACTA METALLURGICA SINICA
Abstract:Microstructure evolutions in the steady-state growth region of directionally so- lidified Ti-43Al-3Si (atomic fraction, %) alloy were studied at growth rates of 3—100 μm/s. There are four main phase transitions during directional solidification: L→Ti5Si3 ,L →α+Ti5Si3, α→α2(Ti3Al)+γ(TiAl) and α2→γ+Ti5Si3, especially, the eutectic reaction of α and Ti5Si3 is the typical solidification behavior. When the growth rate exceeds 20 μm/s, another phase transition of L→γ+Ti5Si3 also happens. With increase of growth rate, the steady-state growth microstructure changes from coarse cells to fine cells, to cellular dendrites and then to dendrites. The Ti5Si3 phase stabilizing α phase distributes in the α matrix at a low growth rate, and in the solidified γ matrix at a relatively high growth rate, which is unfavorable in seeding. When the growth rate is 10 μm/s, the distance needed to reach steady-state region becomes shorter, which is favourable in seeding for the present alloy. KEY WORDS Ti-43Al-3Si alloy, directional solidification, microstructure, steady-state growth
What problem does this paper attempt to address?