Abstract:In this study, a novel sol-gel method is used to synthesize amorphous silica-alumina materials with a narrow mesoporous distribution and various Si/Al molar ratios without using any templates and pore-regulating agents. During the preparation procedure, only inexpensive inorganic salts were used as raw materials, instead of expensive and harmful alkoxides. The precursor sol was dried at room temperature in a vacuum box kept at 60 mmHg until it began to form the gel. The results of a nitrogen sorption experiment indicate that the synthesized materials with different Si/Al molar ratios have similar mesoporous distributions (within 2-12 nm). Moreover, it was found that the material's pore size distribution remains at a similar value during the heat treatment from room temperature to 550 degreesC. On the basis of the nitrogen sorption, TEM, and AFM characterization results, a formation mechanism of mesopores which accounts for the experimental data is also suggested. This suggested mechanism involves rearrangement of the primary particles during the drying process to form the precursors of the similarly sized mesopores. The synthesized materials were characterized by XRD, thermal analysis (TG/DTA), Al-27 and Si-29 MAS NMR spectroscopy, SEM, TEM, and AFM. The results of Al-27 and 29Si MAS NMR indicate that the distribution of silicon and aluminum in the synthesized materials is more uniform and homogeneous than that in the mixed oxides prepared via the traditional sol-gel method even at high alumina contents. The type and density of the acid sites were studied using pyridine adsorption-desorption FTIR spectroscopy. It was shown that the acidity of the synthesized materials is higher than that of the silica-alumina materials prepared by conventional methods.

Synthesis of Multimorphologic Nanostructured SiO 2 Using Organogelator Sol–gel Transcription

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

Synthesis and Gelation Behavior of a Novel Bithiazole Based Low-Molecular-Mass Organic Gelator

Macroporous Sio2 Monoliths Prepared Via Sol-Gel Process Accompanied by Phase Separation

Synthesis, structural and morphological characteristics of (P(MA-MPTMS)/SiO2 hybrid nanocomposites

Micro to mesoporous SiO2xerogels: the effect of acid catalyst type in sol–gel process

Synthesis of the Micro-meso Porous SiO2 Xerogel and Its Physicochemical Properties

Investigation of compound state of SiO2-TiO2 aerogel synthesized through controlled sol-gel reaction

Microgel-Silica Hybrid Particles: Strategies for Tunable Nanostructure, Composition, Surface Property and Porphyrin Functionalization

Hierarchical Structure of SiO2 by In Situ Modification Combining Quartz Sand and Methyltrimethoxysilane

Ultrasonic Synthesis of Silica−Alumina Nanomaterials with Controlled Mesopore Distribution Without Using Surfactants

Self-Assembling Oligo(2-oxazoline) Organogelators for the Encapsulation and Slow Release of Bioactive Volatiles.

Cosolvent-free sol–gel synthesis of macroporous silica gels from tetramethoxysilane–tetraethoxysilane mixtures

Controllable Preparation Of Ultra-Low-Dielectric Nanoporous Silica Via Inorganic-Organic Hybrid Templates

Synthesis and Characterization of Three-Dimensionally Ordered Macroporous Silica

Sustainable synthesis of ordered mesoporous materials without additional solvents

A Systematic Investigation Of The Formation Of Ordered Mesoporous Silicas Using Poly(Ethylene Oxide)-B-Poly(Methyl Methacrylate) As The Template

One-step Synthesis of Highly Monodisperse Hybrid Silica Spheres in Aqueous Solution.

Preparation and Morphology of SiO 2 /PMMA Nanohybrids by Microemulsion Polymerization

SYNTHESIS OF LARGE-PORT HIGH SILICA MOR ZEOLITE BY DRY GEL SELF TRANSFORMATION IN THE ABSENCE OF ORGANIC STRUCTURE-DIRECTING AGENTS

Synthesis of Mesoporous Silica Using the Sol-Gel Approach: Adjusting Architecture and Composition for Novel Applications