Abstract:In this study, precursor decomposition as well as nucleation and growth processes during the preparation of In2O3 powders via chemical precipitation were investigated. This is to provide guidance for the preparation of high-quality In-based oxide target powders. In-situ phase and microstructure evolution during thermal decomposition of precursors were analyzed. In addition, decomposition behavior of precursors at different heating rates was explored. Results show that amorphous In(OH)3 precursor powder gradually decomposes and transforms into crystalline In2O3 powder during heating process. Its degree of crystallinity increases with the increase in temperature. Fine and homogeneous In2O3 powder with average grain size of 54.46 nm was obtained by holding the powder at 770 °C for 3 h. The decomposition of precursors at any given heating rate can be divided into two stages: (i) dehydration and (ii) nucleation and crystallization. However, higher heating rate clearly results in temperature hysteresis effect, the occurrence of decomposition reaction at higher temperature, and an increase in the maximum reaction rate of decomposition reaction. Moreover, activation energy of thermal decomposition was obtained using model-free transformation method. Decomposition reaction model of In(OH)3 precursor was established using model-fitting method. It was deduced that first-stage reaction mechanism is three-dimensional diffusion. Reaction rate in this stage is controlled by product layer diffusion. Furthermore, second-stage reaction mechanism is random nucleation and subsequent growth. Reaction rate in this stage is controlled by nucleation and growth rates.

Synthesis of metastable hexagonal In2O3 nanocrystals by a precursor-dehydration route under ambient pressure

Metastable Hexagonal In2O3 Nanofibers Templated from InOOH Nanofibers under Ambient Pressure

Synthesis and Characterization of Porous Single-Crystal-Like In2O3 Nanostructures Via a Solvothermal-Annealing Route

Synthesis and characterization of In2O3 nanocube via a solvothermal-calcination route

Synthesis and Photoluminescence of Single-Crystalline In2O3 Nanowires

Single-source Approach to the Synthesis of In2S3 and In2O3 Crystallites and Their Optical Properties

Controlled Synthesis of In2O3 Octahedrons and Nanowires

Synthesis And Photocatalytic Activity Of Single-Crystalline Hollow Rh-In2o3 Nanocrystals

Large-scale synthesis of in2O3 nanowires and their characterization

Low-temperature Synthesis of Bi4Ti3O12 Nanocrystals by Hydrothermal Method

One-Step Synthesis of Nearly Monodisperse, Variable-Shaped In<sub>2</sub>O<sub>3</sub>Nanocrystals in Long Chain Alcohol Solutions

Precursor decomposition mechanism of In2O3 powder for oxide ceramic targets

Large-Scale Growth of In2o3 Nanowires and Their Optical Properties

The synthesis of In, In2O3 nanowires and In2O3 nanoparticles with shape-controlled

Corundum-Type Tubular and Rod-Like In2o3 Nanocrystals: Synthesis from Designed Inooh and Application in Photocatalysis

Morphological Evolution of In2O3 Crystallites by Metallothermal Reaction Growth: A Unified Elucidation

Large-scale Synthesis of in 2 O 3 Nanowires

Synthesis, Thermal Stability and Properties of ZnO2 Nanoparticles

A New Metastable Phase of Crystallized V2O4·0.25H2O Nanowires: Synthesis and Electrochemical Measurements

SYNTHESIS OF NANOCRYSTALLINE SnO2 BY PRECIPITATION

Wurtzite-to-Rocksalt Structural Transformation in Nanocrystalline CoO