Abstract:Indium hydroxide (In(OH)(3)) nanorods and Sn-doped indium oxyhydroxide (InOOH) nanoparticles were synthesized through the hydrothermal method in an aqueous solution. Sodium hydroxide (NaOH) was introduced to adjust the pH value, and sodium acetate (CH3COONa) was employed as the inducer to accelerate the growth along the preferential orientation. Cubic In(OH)(3) was synthesized at pH values ranging from 4.0 to 8.0. In(OH)(3) nuclei grows in the direction {100} into nanorods observed from lattice fringes with an interplanar spacing of about 0.403 nm. The SAED pattern of In(OH)(3) nanorods indicates the rodlike nanocrystal is a single crystal which matches well with the characteristic peaks of cubic In(OH)(3) XRD patterns. The FTIR spectrum signifies the absorption of CH3COO- onto the surface of In(OH)(3) nanorods, which accelerate the growth along the direction {100}. Due to the inhibition effect of OH-, In(OH)(3) particles with a smaller aspect ratio and In2O3 particles with a smaller crystal size were synthesized with the increase of pH values. At a high hydrothermal temperature, cubic In(OH)(3) transformed into orthorhombic InOOH owing to the dopant of Sn with a size smaller than In3+ and r(Sn4+)/r(O2-) = 0.58. The lattice fringes and SAED patterns of InOOH and hexagonal In2O3 nanoparticles were determined. It was also observed that the average size increased from 27 to 46 nm when Sn doping content increased from 2% to 10%. The sensors based on the Sn-doped In2O3 nanoparticles showed a fast (6-7 s) and high response (R-a/R-g = 8.9) to 100 ppm acetone at an operating temperature of 280 degrees C. This work provides a preliminary investigation into the effect of sodium acetate and Sn on the growth of In(OH)(3) nuclei.

Metastable Hexagonal In2O3 Nanofibers Templated from InOOH Nanofibers under Ambient Pressure

Synthesis of metastable hexagonal In2O3 nanocrystals by a precursor-dehydration route under ambient pressure

Corundum-Type Tubular and Rod-Like In2o3 Nanocrystals: Synthesis from Designed Inooh and Application in Photocatalysis

Large-Scale Growth of In2o3 Nanowires and Their Optical Properties

InOOH Hollow Spheres Synthesized by a Simple Hydrothermal Reaction.

Synthesis and Photoluminescence of Single-Crystalline In2O3 Nanowires

The synthesis of In, In2O3 nanowires and In2O3 nanoparticles with shape-controlled

Fabrication and Characteristics of In2O3 Nanowires

Biuret-assisted Formation of Nanostructured In2O3 Architectures and Their Photoluminescence Properties

Large-scale synthesis of in2O3 nanowires and their characterization

Preparation of One-Dimensional Diluted Magnetic Semiconducting Cr0.046zn0.954o and Properties Tuning with H-2 Atmospheric Annealing

Synthesis And Photocatalytic Activity Of Single-Crystalline Hollow Rh-In2o3 Nanocrystals

Large-scale Synthesis of in 2 O 3 Nanowires

Synthesis and Characterization of Porous Single-Crystal-Like In2O3 Nanostructures Via a Solvothermal-Annealing Route

Corundum‐Type In2O3 Urchin‐Like Nanostructures: Synthesis Derived from Orthorhombic InOOH and Application in Photocatalysis

Indium Hydroxides, Oxyhydroxides, And Oxides Nanocrystals Series

Nanocrystalline InOOH: Control synthesis and photocatalytic performance in aqueous phase

Preparation of In(OH)(3) and In2O3 Nanorods Through a Novel Hydrothermal Method and the Effect of Sn Dopant on Crystal Structures

Single-source Approach to the Synthesis of In2S3 and In2O3 Crystallites and Their Optical Properties

Fabrication and Photoluminescence Characteristics of Single Crystalline In2O3 Nanowires

Synthesis and characterization of In2O3 nanocube via a solvothermal-calcination route