Large-Sized Smbco Single Crystals With T-C Over 93 K Grown In Atmospheric Ambient By Crystal Pulling

X Yao,T Izumi,Y Shiohara

DOI: https://doi.org/10.1088/0953-2048/16/4/101

2003-01-01

Abstract:Sm1+xBa2-xCu3Oz (SmBCO) single crystals were grown under atmospheric ambient by the top-seeded solution growth method. Inductively coupled plasma results indicate that there is negligible Sm substitution for Ba sites in the grown SmBCO crystals, although they crystallized from different Ba-Cu-O solvents with a wide composition range (Ba/Cu ratio of 0.5-0.6). As a result, these crystals show high superconducting critical transition temperature values (T-c) of over 93 K with a sharp transition width after oxygenation. A large-sized crystal with an a-b plane of 23 x 22 mm(2) and a c-axis of 19 mm was obtained at a high growth rate of nearly 0.13 mm h(-1). In short, with more controllable thermodynamic parameters, SmBCO single crystals can readily achieve both large size and high superconducting properties.