Abstract:In the present study, the effect of Nb addition on mechanical behavior and glass formation in (Zr56Co28Al16)100−xNb(x=0,2,4) bulk metallic glasses was studied. The differential scanning calorimetry (DSC) was used to investigate thermal properties of samples. Further, mechanical behavior of prepared samples was analyzed using quasi-static compressive tests. The results showed that 2 at.% minor addition of Nb enhances the glass forming ability (GFA), but larger amount of Nb (4%) deteriorates GFA. The X-ray diffraction patterns also confirmed that the structures of whole of studied compositions are amorphous. In addition, the compressive test results revealed that 2% addition of Nb significantly improves compressive ultimate strength (up to 2.5 GPa) and increases the plastic strain from 1.1% in the composition having no Nb content to ~ 6%. The observation of shear band branching and also the increase in the density of vein-like patterns in the fracture surface (studied by scanning electron microscopy) also confirm the improvement of plasticity in (Zr56Co28Al16)98Nb2 sample. Our finding highlights the effect of minor alloying on the formation and mechanical properties of bulk metallic glasses.

Formation and Thermal Stability of Ni-Based Bulk Metallic Glasses in Ni-Zr-Nb-Al System

Formation, Thermal Stability and Mechanical Properties of Zr-Nb-Cu-Ni-Al Bulk Metallic Glasses

On the atomic structure of Zr–Ni and Zr–Ni–Al metallic glasses

Glass Forming Ability and Mechanical Properties of New Ni-Based Bulk Metallic Glasses

Formation of Ni–Nb–Zr–X (X = Ti, Ta, Fe, Cu, Co) Bulk Metallic Glasses

Glass-forming ability and corrosion resistance of Zr-based Zr-Ni-Al bulk metallic glasses

Formation, Thermal Stability and Mechanical Properties of Ti42.5Zr7.5Cu40Ni5Sn5 Bulk Metallic Glass

The Glass-Forming Ability of Pr–Ni–Al Bulk Metallic Glasses

Glass-Forming Ability, Mechanical Properties, and Energetic Characteristics of ZrCuNiAlNbHfY Bulk Metallic Glasses

Glass-forming Ability and Thermal Stability of a New Bulk Metallic Glass in the Quaternary Zr–Cu–Ni–Al System

Glass Formability, Thermal Stability and Mechanical Properties of La-Based Bulk Metallic Glasses

Effects of adding niobium on microstructures and mechanical properties of ((Zr40Ti40Ni20)72Be28)100-Nb bulk metallic glasses

Catching the Ni-based Ternary Metallic Glasses with Critical Diameter Up to 3 Mm in Ni–Nb–Zr System

Tuning Glass Formation and Mechanical Properties of ZrCoAl(Nb) Bulk Metallic Glass with Nb Microalloying Process

Quaternary Ti–Zr–Be–Ni Bulk Metallic Glasses with Large Glass-Forming Ability

Thermal Stability and Mechanical Properties of Zr50Ti5Cu18Ni17Al10 Bulk Metallic Glass

Glass-Forming Ability and Mechanical Properties of the Ternary Cu-Zr-Al and Quaternary Cu-Zr-Al-Ag Bulk Metallic Glasses

Incorporation of ultrafine nanograins in Zr–Cu–Al–Ni–Co bulk metallic glass enabling significantly improved mechanical properties

Glass-forming Ability and Crystallization Behavior of Some Binary and Ternary Ni-based Glassy Alloys

The effect of minor alloying on the glass forming ability and crystallization reaction of Ti32.8Zr30.2Cu9M5.3Be22.7 (M=Fe, Co, and Ni) bulk metallic glass

Ni- and Be-free Zr-based bulk metallic glasses with high glass-forming ability and unusual plasticity.