Influence of Buffer Layer on Performance of SOFC Supported by Al2O3-Doped YSZ Electrolyte

Jing Sui,Yu-bao Tang,Jiang Liu

DOI: https://doi.org/10.3321/j.issn:1000-565X.2008.07.010

2008-01-01

Abstract:NiO and La0.8Sr0.2MnO3 were first synthesized by means of glycine-nitrate combustion method and were respectively used as the anode and the cathode materials of solid oxide fuel cell(SOFC).Next,YSZ(8% yttrium-stabilized zirconia) and the YSZ doped with 4% Al2O3 were pressed into wafer and sintered at 1 450 ℃ for 4 h.Then,the anode side of the Al2O3-doped electrolyte was coated with the buffer layer and was further sintered at 1 200 ℃ for 1 h.Moreover,the output performances and AC impedance spectroscopy of the three kinds of fuel cells were tested,with humid hydrogen containing 3% H2O as the fuel and with the ambient air as the oxidant.The results indicate that the cell only doped with Al2O3(Cell 1) is of the worst output performance at 850 ℃,the output power density being 0.083 W/cm2,and that the cell doped with Al2O3 and coated with buffer layer(Cell 2) is of the best output performance at the same temperature,the output power density being 0.120 W/cm2.AC impedance spectroscopy analyses indicate that the interface resistance and Ohmic resistance of Cell 2 are obviously less than those of Cell 1,meaning that insulative nickel aluminum spinel is generated by the reaction of Al2O3 and NiO during the sintering at a high temperature.Therefore,the application of buffer layer not only keeps the contribution of Al2O3 to the electrolyte but also reduces the generation of insulative nickel aluminum spinel.