The study on the reinforcement of filling amount of potassium titanate whisker on the bending strength of dental composite resin

ZHANG Xiu-yin,TIAN Ai-feng,LIU Yi-rong,CHENG Xia,LIU Jun

DOI: https://doi.org/10.3969/j.issn.1009-3761.2009.03.010

2009-01-01

Abstract:Objective: To study the reinforcement of the filling amount of potassium titanate whisker on the bending strength of dental composite resin. Methods: 3% silane coupling agent was used to modify potassium titanate whisker. Then the whisker was filled into resin matrix by hand-mixing, and five groups of resin compound were synthesized with different content of whisker, 40%, 50%, 60% ,70% , and 75%. Specimens were fabricated with standard sizes. Three-point bending strength was tested, and fracture surfaces were observed by electron microscopy. Results: The bending strength of the five groups were (109.85±15.25) MPa, (133.50±21.66) MPa, (145.30±19.63) MPa, (112.15±11.04) MPa, and (112.75± 8.73) MPa respectively. The bending strength with 60% filler mass fraction was maximum. SAS statistical software was used to analyze the results of the 5 groups with Tukey test, the result indicated that the bending strength of 60% group has significant difference with 40%, 70%, 75% groups at the α=0.01 level; while there are no significant differences among the 40%, 50%, 70%, 75% groups at the α =0.05 level. SEM results showed that whiskers were dispersed evenly in the matrix resin and combined well in the groups of 40%, 50% and 60%. Conclusion: The bending strength of composite resin can be increased by potassium titanate whisker. However, too much or too little cannot achieve the best results.