Influences of silica size distribution on the performance of dental composite

Baolei Zhu,Mo Zhu,Ruili Wang,Meifang Zhu,Qinghong Zhang,Bin Sun,Jiao Sun
DOI: https://doi.org/10.3969/j.issn.1004-7565.2011.01.002
2011-01-01
Abstract:Objective The Purpose of this study was to evaluate the influence of the size distribution of the inorganic filler on the performance of the experimental dental composite.Methods Mixture of surface modified micro silica(MS) and nano silica(NS) with different weight ratio were used as the inorganic filler.A series of experimental dental composite with different filler size distribution were obtained by mixing processing of the inorganic filler with dental monomer,and were named as M50N20,M55N15,M58N12,M60N10,M63N07.The relationship of filler size distribtution and filler loading was studied.Three point bending,Vickel's hardness tests were employed to study the filler size distribution on the mechanical properties of the experimental dental composite.Scanning electronic microscopy was employed for the morphology analysis for the cross section of the composite.Results It was found that the filler loading mainly denpends on the surface area and the compact density of the silica filler,the composite with 58/12 of MS/NS reached 84wt% filler loading.The mechanical tests showed that the filler distribution had obvious effects on the flexural strength and vicker hardness of the composite.Sample M58N12 reached the highest flexural strength(153.2 MPa) and vicker hardness(102.3MPa).The morphology analysis with SEM on the composite showed that nano silica had better bonding with the resin matrix.Significance This study shows that the filler size distribution has a significant influence on the mechanical properties and filler loading of the dental composite.
What problem does this paper attempt to address?