Abstract:An eco-friendly synthetic route was developed for the formation of nickel oxide (NiOaq and NiOet) nanoparticles (NPs) by treating Ni(NO3)2.6H2O with aqueous/ethanolic extracts of Elettaria cardamomum leaves; the same reaction was performed in the presence of graphene oxide (GO) to produce NiOaq@GO and NiOet@GO nanocomposites (NCs), respectively. The NMs were characterized by XRD, FT-IR, SEM, EDX, UV-visible spectroscopy, and TGA-DSC analysis. They were also subjected to electrochemical investigations and photocatalytic degradation of crystal violet (CV) dye. XRD analysis revealed the average crystallite sizes of 8.84-14.07 nm with a face-centered cubic form of NiO NPs and a hexagonal structure of their nanocomposites with GO. FT-IR spectroscopy confirmed the presence of Ni-O vibrations at 443-436 cm-1. SEM images confirmed the spherical morphology of NiO NPs while NiOaq@GO NCs contained randomly aggregated, thin, and wrinkled graphene sheets. NiOaq and NiOet have shown particle sizes of 27.7-30.63 nm which were decreased to 19.33-26.39 nm in their respective NiOaq@GO and NiOet@GO NCs. EDX spectra verified the homogeneous distribution of elements (Ni, O, C) on the surface of the particles. The synthesized NCs have shown smaller band gaps (NiOaq@GO = 3.74 eV; NiOet@GO = 3.34 eV) as compared to their respective NPs (NiOaq = 5.0 eV; NiOet = 3.89 eV). TGA/DSC data was used to find the thermal stabilities, glass transition temperatures, and enthalpies. Cyclic voltammetry measurements exhibited distinct oxidation and reduction peaks. NCs exhibited better potential as electrode materials for supercapacitor applications as compared to their respective NPs. NiOet@GO exhibited the best electrochemical performance and photocatalytic degradation efficiency of CV dye. After 120 min exposure to sunlight, the degradation coefficient of CV was observed to be 82.93, 86.34, 89.99, 90.27 and 81.65 % in the presence of NiOaq, NiOet, NiOaq@GO, NiOet@GO and GO, respectively.

Synthesis of NiO nanoparticles in ethylene glycol

Synthesis of Nickel Nanopowders in Ethylene Glycol

PREPARATION OF NiO NANOPARTICLES ON THE SILICA SURFACE BY ADSORPTION PHASE SYNTHESIS AND ITS REGULATION ON MORPHOLOGY OF NiO PARTICLES

Synthesis of iron–nickel nanoparticles via a nonaqueous organometallic route

Synthesis of Ni-Sio2 Composite Microspheres in Situ in Ethylene Glycol

Synthesis of Ni Nanopowders Using an EHA System

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

Synthesis of Colloidal Nio Nanocrystals by A Hot-Injection Approach with A Protecting Ligand

Synthesis and Characterization of Cu-Ni Composite Nanoparticles in Ethylene Glycol

Experimental Study on Synthesis of Nio Nano-Particles

Synthesis, magnetic and adsorption of dye onto the surface of NiO nanoparticles

Synthesis of nickel oxide nanoparticles by Sol-gel method

Synthesis of NiO nanowires by a sol-gel process

Green synthesis of NiO and NiO@graphene oxide nanomaterials using Elettaria cardamomum leaves: Structural and electrochemical studies

Synthesis and performances of nano-sized neodymium oxide

Preparation and characterization of nanocrystalline NiO in mixed solvent

Selective Synthesis of α-Nickel Hydroxide through a Polyol Process

Preparation of Ethylene Glycol Via Catalytic Hydration with Highly Efficient Supported Niobia Catalyst

Preparation of nickel nanopowders in ethanol-water system (EWS)

One pot synthesis of Ag nanoparticle modified ZnO microspheres in ethylene glycol medium and their enhanced photocatalytic performance

Synthesis and characteristics of NiO nanoparticles by thermal decomposition of nickel dimethylglyoximate rods