Glycol Production from Sorbitol Hydrogenolysis over Hydrothermally Stable Ni Catalysts and the Mechanistic Study
Xinyu Zhu,Xindi Feng,Chang Yao,Weixiao Sun,Jianbo Ma,Fuzeyu Zhong,Jianrong Zeng,Xiaohu Ge,Wenyao Chen,Gang Qian,Xuezhi Duan,Yueqiang Cao,Zhen Liu,Xing-Gui Zhou,Jing Zhang
DOI: https://doi.org/10.1021/acs.iecr.4c00671
2024-01-01
Industrial & Engineering Chemistry Research
Abstract:Hydrogenolysis of sorbitol can produce value-added glycols (ethylene glycol and 1,2-propanediol), which are widely used as antifreezes and monomers for polyester fibers. Although Ni-based catalysts have advantages in low cost, high selectivity, and high activity, they are susceptible to sintering and leaching under hydrothermal conditions. Here, Ni on well-mixed oxides (Ni/MgaAl(10-a)O(x)) derived from layered double hydroxide (LDH) precursors were successfully synthesized and then evaluated in the aqueous-phase hydrogenolysis of sorbitol at 250 degrees C. A total glycol yield of 43.8% was obtained at a sorbitol conversion of 97.9% using Ni/Mg6Al4Ox. Notably, the activity of Ni/Mg6Al4Ox was maintained during the recyclability test, with minimal sintering and leaching. On the contrary, the Ni/Al2O3 and Ni/MgO catalysts made by conventional coprecipitation suffered severe deactivation, sintering, and leaching. The reduction of the NiMgAl-LDH precursor led to the formation of highly dispersed Ni on well-mixed oxides. The largely improved hydrothermal stability may be due to enhanced metal-support interactions derived from the NiMgAl-LDH precursor. Density functional theory calculations suggest that 1,2-propanediol formation is likely to proceed via the dehydration of glyceraldehyde instead of dihydroxyacetone, and the rate-determining step is the formation of glyceraldehyde and dihydroxyacetone during the retro-aldol condensation of ketohexose.