Abstract:Nano-cobalt materials play an important role in the hydrogenation of ethyl lactate to 1,2-PDO.Herein,Co3O4 nanomaterials with different morphologies were synthesized,which were further reduced under hydrogen atmosphere to form nano-cobalt.The TEM results indicated that nano-cobalt materials obtained from Co3O4 at a low temperature kept original morphologies.The TPR results showed that the Co3O4 nanoparticles reduced at a low temperature were easier to generate metal cobalt than Co3O4 nanorods.Hence,cobalt nanoparticles gave an excellent conversion for the hydrogenation of ethyl lactate while cobalt nanorods had no activity.Furthermore,the effect of reduction temperature of Co3O4 on the nano-cobalt crystal structures was investigated.XRD and TEM results showed that the hcp phase can be produced at a lower temperature.With increasing the reduction temperature,the transformation from hcp phase to fcc phase would take place.The effect of cobalt nanoparticles reduced at different temperature on the performance of hydrogenation of ethyl lactate was studied.Experiments proved that the cobalt nanoparticles had a positive effect on the hydrogenation performance till the reduction temperature increased to 300 ℃ with a 71％ conversion of ethyl lactate.However,when the reduction temperature increased continually,the conversion of ethyl lactate decreased.It indicated that the hcp phase was beneficial to the hydrogenation of ethyl lactate while the fcc phase hampered the hydrogenation of ethyl lactate.In addition,aggregation may also lower the catalytic activity above 300 ℃.

Synthesis of cobalt nanoparticles in ethanol hydrazine alkaline system (EHAS) at room temperature

A Hydrothermal Reduction Route to Single‐Crystalline Hexagonal Cobalt Nanowires

Reaction kinetics of reduction of Co2+ by hydrazine in solution for the preparation of cobalt nanoparticles

Synthesis of Cobalt Disulfide Nanoparticles in Polymer Matrix

Growth of Dendritic Cobalt Nanocrystals at Room Temperature

Hydrothermal Synthesis of Cobalt Particles with Hierarchy Structure and Physicochemical Properties

Hydrothermal synthesis of cobalt phosphide nanoparticles

Preparation of monodispersed cobalt–boron spherical nanoparticles and their behavior during the catalytic decomposition of hydrous hydrazine

Aqueous-phase Fischer-Tropsch synthesis catalyzed by cobalt nanoparticles

Cobalt nanoparticles prepared in faujasite zeolites by borohydride reduction

Synthesis and Magnetic Properties of Nearly Monodisperse CoFe2O4Nanoparticles Through a Simple Hydrothermal Condition.

Synthesis of ferromagnetic single-crystalline cobalt nanobelts via a surfactant-assisted hydrothermal reduction process

Cobalt Ferrite Nanoparticles Prepared by Coprecipitation/Mechanochemical Treatment

Electrochemical preparation of cobalt hexacyanoferrate nanoparticles under the synergic action of EDTA and overoxidized polypyrrole film

Hydrothermal Synthesis Of Cobalt-Basic-Carbonate Nanobelts

Synthesis and Characterization of Structure Controlled Nano-cobalt Particles

Sonochemical synthesis, structural and magnetic properties of air-stable Fe/Co alloy nanoparticles

Reduction of Co3O4 by Hydrogen to Prepare Nano-Cobalt and the Study of Hydrogenation of Ethyl Lactate

Solvothermal synthesis and characterization of cobalt sulfide nanocrystals

Synthesis and Magnetic Properties of FeCo Alloy Nanoparticles by Hydrogen Plasma Metal Reaction

Molecule-Based Cobalt Hexacyanoferrate Nanoparticle： Synthesis, Characterization, and Its Electrochemical Properties