Abstract:This paper reports the synthesis of semiconductor nanocrystals of PbS through a facile and inexpensive synthetic route between lead acetate [Pb(Ac)2·3H2O] and dithioglycol (HSCH2CH2SH) without any surfactant. The products were characterized by x-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), Raman spectroscopy, x-ray photelectron spectroscopy (XPS) and infrared (IR) spectroscopy. The size of cube-shaped PbS nanocrystals can be controlled by changing the relative amount of Pb(Ac)2·3H2O and dithioglycol. Smaller cube-shaped PbS nanocrystals were obtained at higher sulfur content in the reaction system. The nanometre-sized single crystals of PbS measure ~83 nm × 59 nm × 22 nm and 39 nm × 10 nm × 7 nm, for lead acetate:dithioglycol ratios of 1:0.375 (denoted as PbS-1) and 1:1.5 (denoted as PbS-2), respectively, when a mixture of NaOH solution of lead acetate and ethyl alcohol solution of dithioglycol is maintained at 220 °C for 4 h in a Teflon-lined autoclave. XRD patterns and HRTEM images confirm the crystalline structure of the PbS crystals. TEM helped to determine the dimension of the single crystals. Raman, XPS and IR helped to further demonstrate the purity of the as-synthesized samples. The optical absorption spectra of suspensions of the these crystals in glycol show shifts in absorption band edge for as-prepared sample PbS-1 from 246 to 271 nm and for PbS-2 from 246 to 275 nm, after four days of storage, respectively. The photoluminescence peaks from the two samples are located at 434 and 433 nm for photoexcitation radiation of 315–355 nm, thus exhibiting a Stokes shift compared with band edge energy. The principal contribution of this work is that the nanometre-size PbS single crystals are prepared without using a surfactant or templating agent. The formation of a five-membered ring via the chelation between the Pb2+ ion and dithioglycol is considered to be crucial in this mechanism.

Nanocubes of PbS with visible luminescence synthesized by sulfonated polymer as stabilizer and modifier at room-temperature

Growth and photoluminescence properties of PbS nanocubes

Controlled Synthesis of Luminescent Cuins2 Nanocrystals and Their Optical Properties

Size-Tunable Near-Infrared Pbs Nanoparticles Synthesized From Lead Carboxylate And Sulfur With Oleylamine As Stabilizer

Synthesis and Electrogenerated Chemiluminescence of PbS Nanospheres.

Synthesis and evolution of PbS nanocrystals through a surfactant-assisted solvothermal route.

Ultrasound-assisted synthesis of PbS quantum dots stabilized by 1,2-benzenedimethanethiol and attachment to single-walled carbon nanotubes

A room temperature chemical route to nanocrystalline PbS semiconductor

Controllable synthesis, characterization and optical properties of colloidal PbS/gelatin core-shell nanocrystals

Synthesis and Optical Property of PbSe Nanocubes Via a Facile Organic Solvent Route

High Yield Synthesis of PbS Nanocubes Using One-Step Solid-State Reaction in the Presence of an Anionic Surfactant

Liquid-liquid interfacial synthesis of single-crystalline PbS nanoplates and nanocube-based microspheres

Room Temperature Synthesis of PbS Nanocrystals with Different Morphologies in PEO–PPO–PEO Triblock Copolymers

Synthesis of Near Infrared Pbs Quantum Dots by Pyrolysis of Organometallic Sulfur Complex

Growth of PbS crystals from nanocubes to eight-horn-shaped dendrites through a complex synthetic route

Synthesis and the Growth Mechanism of PbS Nanorod

L-Cysteine-Assisted Synthesis of PbS Nanocube-Based Pagoda-like Hierarchical Architectures

Controlled Synthesis of Semiconductor PbS Nanocrystals and Nanowires Inside Mesoporous Silica SBA-15 Phase

Synthesis and Characterization of PbS Crystals Via a Solvothermal Route

Morphology Control of Pbs Nanocrystals by A Novel Hydrothermal Process

One-dimensional Growth of Rock-Salt PbS Nanocrystals Mediated by Surfactant/polymer Templates