Characterization of Protective Surface Films on Molten AZ91D Magnesium Alloy Formed in Air and SF6 Protective Gas
Shu-hong NIE,HU-Bo,Shou-mei XIONG,Bai-heng LIU
DOI: https://doi.org/10.3969/j.issn.1001-1560.2005.08.001
2005-01-01
Abstract:With a view to the fact that the casting and melting of magnesium and its alloy are generally carried out in the protective gas SF_6, scanning electron microscopy, transmission electron microscopy, and X-ray diffraction were used to analyze the characteristics of the surface film on AZ91D magnesium alloy molten in air/SF_6 protective gas. It was found that the protective surface film was composed of two layers. Namely, the upper layer was composed of a large amount of loose polycrystalline MgO, a little amount of aluminum oxide, and trace fluoride; and the inner layer was composed of crystalline MgF_2. The atomic ratio of F/O in the surface film increased evidently and so did the surface roughness with increasing exposure time. The reaction between magnesium and fluorine was dominant as the film thickness exceeded a certain value. Moreover, some white flakes composed of MgO and a little amount of MgF_2, with varied size and disperse distribution, existed on the film surface. There existed semicircular discontinuous F-rich white spots composed of about 70% fluorine in some near surface zones, and the F content in the area excluding the white spots was greatly reduced. Since the atomic ratio of F/Mg in the F-rich area was higher than 2/1, that of MgF_2, it could be supposed that the fluorine might diffuse from the protective atmosphere to the bulk melt of AZ91D magnesium alloy through the F-rich zone.