Abstract:Synthesis and phase transformation of nanosized titania has been paid great attention for decades. Nanoparticls of anatase and rutile with various sizes and morphologies were prepared herein in various acidic aqueous solutions via sol-hydrothermal reactions. Anatase forms first and then transforms to rutile in a certain medium. The transformation can be accelerated in acidic solution. However, the strong chemical coordination of some anions, such as CH3COO- (OAc-) and SO42- to titanium suppresses the phase transformation. Thus, phase-pure anatase was formed in either H2SO4 or HOAc aqueous solutions, and phase-pure rutile was formed in HCl solution, especially in concentrated HCl solutions. The phase transformation could also be facilitated by the presence of some minelizer or initial rutile particles. Besides the crystallographic structure, the size and shape of titania could be controlled in solution. Monodisperse anatase nanocrystals were prepared in solvothermal system, which shows high photocatalysis in the decomposition of organic compounds. As microemulsion approach can confine crystal growth and lead to the yield of monodisperse nanoparticles, microemulsion-mediated hydrothermal synthesis to prepare nanoparticles of titania was proposed here. The initial shape of microemulsions of amorphous titania show crucial effect on the eventual shape of nanocrystals of titania. The reverse micelles can confine the growth of nanocrystallites in cores, while the micelles can serve as templates to direct the generation of nanoporous materials. Mesoporous titania with anatase framework was constructed through alkylamine as surfactant in aqueous solution. Upon removal of surfactants, the porous materials exhibit reversible adsorption-desorption isotherms, indicating uniform pore sizes, which would find wide application in photocatalysis. Under hydrothermal condition, the mesoporous titania can be transformed into finely dispersed nanoparticles of anatase and rutile, respectively.

Sol-Hydrothermal Synthesis And Hydrothermally Structural Evolution Of Nanocrystal Titanium Dioxide

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Phase formation and transformation of nanostructured titania in solution

Comparative Sol–Hydro(Solvo)thermal Synthesis of TiO2 Nanocrystals

Hydrothermal Preparation of Uniform Nanosize Rutile and Anatase Particles

Hydrothermal Preparation of Nano Titanium Dioxide Materials

Hydrothermal Synthesis and Characterization of Nanocrystalline Anatase Titania from Ti(OC<sub>4</sub>H<sub>9</sub>)<sub>4</sub>

Hydrothermal Synthesis of Nanocrystalline Anatase Titanium Dioxide Particles

Preparation of Nanocrystalline Anatase Tio2 Using Basic Sol-Gel Method

Control of Microscopic Morphology and Structure of One Dimensional Titanium Dioxide Nanomaterials

Hydrothermal synthesis and photocatalytic property of CaTiO 3 assisted with sodium citrate

Influence of solution concentration on the hydrothermal preparation of titania crystallites

Supercritical Hydrothermal Synthesis of Titanium Dioxide Nanostructures with Controlled Phase and Morphology

Microemulsion-Mediated Hydrothermal Synthesis and Characterization of Nanosize Rutile and Anatase Particles

Solvothermal Synthesis of Nanosized Tio2 Particles with Different Crystal Structures and Their Photocatalytic Activities

Synthesis, characterization and study of the structural change of nanobelts of TiO2 (H2Ti3O7) to nanobelts with anatase, brookite and rutile phases

Synthesis of nanocrystalline rutile titania by Co-thermal hydrolysis of TiCl4 and TiCl3 solutions

Lattice Deformation and Phase Transformation from Nano-Scale Anatase to Nano-Scale Rutile TiO2 Prepared by a Sol-Gel Technique

Preparation and investigation of TiO2 Sol containing nanometer anatase crystalline grains

Low temperature synthesis and mechanism of finely dispersed nanorod rutile titanium dioxide