Abstract:Without use of any templates or shape-protectors, uniformly sized anatase TiO2 nanocrystallites with cuboidal morphology were synthesized by changing titanium hydroxide precipitates into their corresponding ethanol-gels (viz. by washing several times with anhydrous ethanol) followed by drying in supercritical ethanol (7.0MPa, 270°C) and calcination at high temperature (AS-preparation). Characterizations with X-ray diffraction (XRD), Raman spectroscopy and nitrogen adsorption suggest that the cuboidal anatase nanocrystallites are highly resistant to thermal sintering. The anatase structure of the cuboidal nanocrystallites was maintained even after calcinations up to temperatures as high as 800°C. Thermogravimetric (TG) measurements in flowing air show that the as-prepared cuboidal TiO2 nanocrystallites were contaminated with some carbonaceous residues, which can be completely removed by calcination at 500°C in air. Application of these cuboidal TiO2 nanocrystallites as photocatalytic materials was evaluated by photocatalytic degradation of methyl orange in water. With increasing the calcination temperature up to 800°C, the photocatalytic activities of anatase TiO2 cuboids increased gradually due to improved crystallization of the material. The sample calcined at 800°C afforded the highest photocatalytic activity, which is comparable to that of the commercial photocatalyst Degussa P-25. Due to the presence of carbonaceous residues after the supercritical drying in the preparation, the samples calcined at temperatures no higher than 400°C showed higher photocatalytic activities than the sample calcined at 500°C. However, further calcination of the sample at 1000°C led to drastic reduction in the photocatalytic activity due to the anatase-to-rutile phase transformation and sintering of the material.

Hydrothermal Synthesis and Characterization of Nanocrystalline Anatase Titania from Ti(OC<sub>4</sub>H<sub>9</sub>)<sub>4</sub>

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Direct Continuous Hydrothermal Synthesis of High Surface Area Nanosized Titania

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Synthesis and characterization of nanosized anatase TiO2 cuboids

Control of Microscopic Morphology and Structure of One Dimensional Titanium Dioxide Nanomaterials

Hydrothermal Synthesis and Photocatalytic Property of CaTiO_3 Assisted with Sodium Citrate

Hydrothermal synthesis and photocatalytic property of CaTiO 3 assisted with sodium citrate

Synthesis and photocatalytic properties of nano bi-crystalline titania of anatase and brookite by hydrolyzing TiOCl2 aqueous solution at low temperatures

Crystallization of Anatase from Amorphous Titania in Hot Water and in Vitro Biomineralization.

Preparation of Anatase-Type TiO_2 Nanoparticals from Ti (SO4)2 Solution under Hydrothermal Conditions and Its Photocatalytic Performance

Hydrothermal Synthesis of Titania Powder with Different Particle Sizes

Hydrothermal Preparation of Uniform Nanosize Rutile and Anatase Particles

A Simple Solution-Phase Route for Room-Temperature Synthesis of Mesoporous and Nanocrystalline Anatase Tio2

Preparation and Characterization of Nanosized Anatase TiO2 Cuboids for Photocatalysis

Titania Nanoflowers with High Photocatalytic Activity

PREPARATION OF ANATASE TiO2 SOL AND POWDER BY SOLVOTHERMAL SYNTHESIS

Preparation of Anatase TiO2 Nanocrystalline and Research on Origion of Phase

One-pot Hydrothermal Synthesis of the Dual-Phase Anatase/tio2-B Nanoparticles with K2Ti6O13 Nanofibers for Enhanced Photocatalysis