Effect of LiSbO3 and SrZrO3 doping on the piezoelectric properties and microstructural behavior of K0.5Na0.5NbO3 ceramics
Wooseop Shin,Sumi Kim,Eunji Kim,Dokyum Kim,Seong-Uk Oh,Jung-A Lee,Young-Woo Heo,Joon-Hyung Lee,Sahn Nahm
DOI: https://doi.org/10.1007/s43207-023-00356-8
IF: 2.506
2024-01-19
Journal of the Korean Ceramic Society
Abstract:The effect of LiSbO 3 and SrZrO 3 doping on the piezoelectric characteristics of K 0.5 Na 0.5 NbO 3 -based ceramics was studied. First, (1 − x)K 0.5 Na 0.5 NbO 3 –xLiSbO 3 –CuO (0.00 ≤ x ≤ 0.07) was synthesized and a single phase of perovskite was observed in the range of 0.00 ≤ x ≤ 0.05. As LiSbO 3 content increased, the orthorhombic single phase changed to orthorhombic and tetragonal multiphase. T O–T decreased from 176 °C (x = 0.00) to 85 °C (x = 0.05) and, the d 33 showed the highest value of 156 pC/N (x = 0.05). Next, (0.95K 0.5 Na 0.5 NbO 3 –0.05LiSbO 3 )–xSrZrO 3 –CuO (0.00 ≤ x ≤ 0.05) was studied. All compositions were well synthesized as perovskite phases; orthorhombic and tetragonal mixed phases up to x = 0.02, rhombohedral, orthorhombic, and tetragonal mixed phases at x = 0.03 and 0.04; and rhombohedral and tetragonal phases at x = 0.05. T O–T decreased from 78 °C (x = 0.00) to 32 °C (x = 0.04), and T R–T was formed at 48 °C (x = 0.05). The d 33 value at x = 0.04 was 288 pC/N and significantly reduced to 134 pC/N at x = 0.05.
materials science, ceramics