Exploiting Laser Based Methods for Low-Temperature Solid-State Synthesis: Growth of a Series of Metastable (Sr1-Xmx)1-.delta.cuo2 Materials

CM NIU,CM LIEBER

DOI: https://doi.org/10.1021/ja00054a019

IF: 15

1993-01-01

Journal of the American Chemical Society

Abstract:Pulsed laser deposition (PLD) has been used to prepare a series of (Srl-xCax)l-deltaCuO2 thin film materials on [100] SrTiO3 and [100] MgO at low temperatures. X-ray diffraction (XRD), electron diffraction (ED), and ion-channeling studies have shown that all of the (Srl-xCax)l-deltaCuO2 materials (x = 0-1; delta = 0.1) grown on [100] SrTiO3 at 500-degrees-C have a layered, tetragonal structure with the c-axis oriented perpendicular to the substrate surface. In contrast, the target materials prepared by conventional high-temperature techniques have an orthorhombic structure (x = 0, delta = 0) or consist of multiple phases (x = 0, delta = 0.1; x > 0, delta = 0, 0.1). Rutherford backscattering studies have shown that the composition of the materials prepared by PLD are the same as the starting target stoichiometry, even when the targets contain multiple phases. The dependence of the product structure on growth temperature and substrate lattice constant were also determined. SrCuO2 materials grown at 500, 600, and 700-degrees-C exhibit a decreasing ratio of tetragonal/orthorhombic phase as the temperature increases. These results show that low-temperature growth traps the layered, tetragonal phase. Comparison of the SrCuO2 Structures obtained on [100] SrTiO3 and [100] MgO substrates have also shown that product-substrate lattice matching is important in stabilizing the tetragonal phase and in orienting the crystallographic growth direction. In addition, the physical properties of these new materials have been characterized by electrical and magnetic measurements. The stoichiometric (Srl-xCax)l-deltaCuO2 materials were found to be insulators. However, the nonstoichiometric (Srl-xCax)l-deltaCuO2 materials exhibited systematic increases in conductivity with decreasing x. Furthermore, the x = 0 material, Sr0.9CuO2, showed a transition to a zero resistance state with an onset of almost-equal-to 20 K. The implications of these studies to copper oxide superconductors are discussed.