Abstract:Cross-linked monodisperse polystyrene microspheres were synthesized using one-step method by combining dispersion polymerization with hydrothermal process using styrene as monomer, AIBN as initiator, PVA as stabilizer and ethanol and deionized water as solvent in this paper. The cross-linked monodisperse polystyrene microspheres could be prepared in a large alcohol-water range, even if the crosslinking agent was up to 2 wt%. We focused on the system that the ethanol/water ratio of solvent was fixed at 50/50, to study the effects of stabilizer type and content, organic phase content, initiator concentration and autoclave fill volume on the morphology of the microspheres and size distribution. It was found that the microspheres showed coalescence with decreasing the molecular weight and increasing content of stabilizer. Even without any stabilizers the monodisperse crosslinked PS microspheres could still be prepared when high content crosslink agent was used. The microspheres showed polydispersity gradually with the organic phase increasing. The content of the initiator and the fill volume in the autoclave have little effect on the morphology of the microspheres. And the cause and mechanism of the one-step preparation method of monodisperse crosslinked polystyrene microspheres were also discussed.

Synthesis of Large-sized Polystyrene Microspheres by Dispersion Polymerization in High Monomer Concentration and Non-aqueous

Synthesis of Polystyrene Microspheres Via Dispersion Polymerization and Its Growth Mechanism

Preparation of Large Particle Size Monodispersed Polystyrene Microspheres with High Crosslinked Degree

Preparation of Large Mono-Disperse Polystyrene Micro-Spheres by Dispersion Polymerization

PREPARATION OF MONODISPERSE CROSS-LINKED POLYSTYRENE MICROSPHERES BY COMBINING DISPERSION POLYMERIZATION WITH HYDROTHERMAL PROCESS

Preparation of micron-size crosslinked microspheres by dispersion copolymerization of polystyrene/2,2′-oxy-bisethanol diacrylate

Synthesis of Monodisperse Crosslinked Polystyrene Microspheres Via Dispersion Copolymerization with the Crosslinker‐postaddition Method

Monodisperse Polystyrene Microspheres Prepared by Dispersion Polymerization with Microwave Irradiation

Preparation of Highly Crosslinked Monodisperse Poly(Styrene-Co-Divinylbenzene)Microspheres by Two-Stage Dispersion Polymerization

Preparation of Mondisperse Crosslinked Polystyrene Microspheres with Micron Size

Controllable Preparation of Monodisperse Polystyrene Microspheres with Different Sizes by Dispersion Polymerization

Study on the Preparation of Monodisperse Polystyrene Microspheres with Narrow Size Distribution

Preparation of Narrow Size Distribution Crosslinked Polystyrene Microspheres

Preparation of Monodisperse Hollow Core Polymer Microspheres via Two-step Dispersion Polymerization

Preparation of Micron-sized Monodisperse Poly (Styrene-Co-methyl Methacrylate) Microspheres by Dispersion Copolymerization

Research on Preparation of Monodisperse Polystyrene Microspheres

Preparation of Surface-Modified Monodisperse Polystyrene Microspheres with Cationic Functional Comonomer

Preparation of Poly(methyl Methacrylate-Co-styrene) Microspheres by Dispersion Copolymerization

Preparation and Superficial Properties of Monodisperse Copolymer Microspheres

STUDY ON PREPARATION OF MONODISPERSE POLYSTYRENE MICROSPHERES WITH DESIGNABLE SIZE

Synthesis and Formation Mechanism of Large-Size Monodisperse P(Glycidyl methacrylate-Styrene) Microspheres by Batch Dispersion Copolymerization