Abstract:The traditional seed preparation method of polystyrene was improved. Firstly, low molecular weight polystyrene seed microspheres with molecular weight of about 10,000 were successfully prepared by adding copolymer inhibitor and adjusting initiator azodiisobutyronitrile. Then, the polystyrene-divinylbenzene microspheres with large particle size were successfully prepared by the method of seed swelling polymerization, using divinylbenzene as crosslinking agent. Polystyrene-divinylbenzene polymer microspheres were characterized by scanning electron microscopy and gel permeation chromatography. The results showed that the molecular weight of polystyrene seed microspheres decreased with the increase of initiator AIBN dosage. Catechol and potassium iodide could significantly reduce the molecular weight of polystyrene seed microspheres. The size of the expanded microspheres prepared from low molecular weight seeds was controllable (up to 10 mu m), with uniform particle size distribution and good monodispersity. Large size polystyrene-divinylbenzene microspheres can be used as stationary phase filler for reversed-phase chromatography, and have a good effect in the purification of industrial phytol. Sulfonated-polystyrene-divinylbenzene can be used as hydrophilic chromatographic filler to separate inosine and uridine. In addition, the baseline separation of cytosine, uracil and thymine was successfully achieved by sulfonated-polystyrene-divinylbenzene column in sodium phosphate buffer/acetonitrile mobile phase.

Preparation of Narrow Size Distribution Crosslinked Polystyrene Microspheres

Preparation of Large Particle Size Monodispersed Polystyrene Microspheres with High Crosslinked Degree

Preparation of Monodisperse Polystyrene Microspheres for Anisotropic Conductive Film

Preparation of micron-size crosslinked microspheres by dispersion copolymerization of polystyrene/2,2′-oxy-bisethanol diacrylate

Synthesis of Monodisperse Crosslinked Polystyrene Microspheres Via Dispersion Copolymerization with the Crosslinker‐postaddition Method

Preparation of Highly Crosslinked Monodisperse Poly(Styrene-Co-Divinylbenzene)Microspheres by Two-Stage Dispersion Polymerization

Preparation of Microsized Crosslinked Microspheres by Dispersion Copolymerization of Polystyrene/polyethylene Glycol 200-Dimethacrylae

Preparation of Mondisperse Crosslinked Polystyrene Microspheres with Micron Size

Preparation of Large Mono-Disperse Polystyrene Micro-Spheres by Dispersion Polymerization

Study on the Preparation of Monodisperse Polystyrene Microspheres with Narrow Size Distribution

Controllable Preparation of Monodisperse Polystyrene Microspheres with Different Sizes by Dispersion Polymerization

Narrow‐disperse, Cross‐linked Polymer Microspheres by One‐step Dispersion Polymerization with a Chain Transfer Agent

PREPARATION OF MONODISPERSE CROSS-LINKED POLYSTYRENE MICROSPHERES BY COMBINING DISPERSION POLYMERIZATION WITH HYDROTHERMAL PROCESS

Research on Preparation of Monodisperse Polystyrene Microspheres

STUDY ON PREPARATION OF MONODISPERSE POLYSTYRENE MICROSPHERES WITH DESIGNABLE SIZE

Preparation of Surface-Modified Monodisperse Polystyrene Microspheres with Cationic Functional Comonomer

Preparation and Modification of Monodisperse Large Particle Size Crosslinked Polystyrene Microspheres and Their Application in High Performance Liquid Chromatography

Preparation of Hollow Microspheres by Dispersion Polymerization-Seeded Swelling Polymerization

Preparation and Characterization of Cyclodextrin-Mediated Polystyrene Microspheres

Preparation of Monodisperse Porous St/DVB Copolymer Microspheres

Preparation and characterization of polystyrene microspheres in the presence of β-cyclodextrin